• Photonics Research
  • Vol. 9, Issue 3, 324 (2021)
Ziyan Jia1, Zeng Chen2, Xu Chen1, Jizhong Yao3, Buyi Yan3, Rui Sheng3, Haiming Zhu2, and Yang (Michael) Yang1、*
Author Affiliations
  • 1State Key Laboratory of Modern Optical Instrumentation, College of Optical Science and Engineering, Zhejiang University, Hangzhou 310058, China
  • 2Center for Chemistry of High-Performance & Novel Materials, Department of Chemistry, Zhejiang University, Hangzhou 310058, China
  • 3Hangzhou Microquanta Semiconductor Inc., Hangzhou 311121, China
  • show less
    DOI: 10.1364/PRJ.416229 Cite this Article Set citation alerts
    Ziyan Jia, Zeng Chen, Xu Chen, Jizhong Yao, Buyi Yan, Rui Sheng, Haiming Zhu, Yang (Michael) Yang. 19.34 cm2 large-area quaternary organic photovoltaic module with 12.36% certified efficiency[J]. Photonics Research, 2021, 9(3): 324 Copy Citation Text show less

    Abstract

    In this study, a quaternary blending strategy was applied in the fabrication of organic photovoltaic devices and large-area modules. As a result, the ultimate quaternary organic solar cells (OSCs) deliver 16.71% efficiency for small-area devices and 13.25% for large-area (19.34 cm2) modules (certified as 12.36%), which is one of the highest efficiencies for organic solar modules to date. Our results have proved the synergistic effects of multiple components in OSCs, providing an effective strategy for achieving high-performance organic photovoltaic devices and modules.

    1. INTRODUCTION

    Donor–acceptor organic solar cells (OSCs) have achieved tremendous progress since the reports of bulk-heterojunction (BHJ) organic solar cells [1]. Early in its development, fullerenes and their derivatives led to an era of OSCs due to their excellent electron mobility, large electron acceptability, and isotropy of charge transport [24]. However, the inherent huge energy losses and weak photon-harvesting capacities of fullerenes limited their further applications [5,6]. Compared with fullerene acceptors, the non-fullerene acceptors (NFAs) usually have strong absorption in the near-infrared region (NIR), and their energy levels can be easily adjusted to match the donors, which have been proved to promote the power conversion efficiencies (PCEs) of OSCs [712]. Driven by the vigorous development of materials science, the PCEs of single-junction OSCs have recently exceeded 17% [1321]. Despite the impressive achievements made by NFAs, the single NFA usually suffers from incomplete absorption of the solar spectrum and relatively low charge mobility compared with perovskite components [22]. In order to make full use of the advantages of fullerene and NFAs, multicomponent blending is recommended to construct multiple devices. The incorporation of fullerene and NFAs into the BHJ layer provides a promising approach to improve the photovoltaic performance of OSCs.

    The recent rapid progress of OSC materials, especially NFAs with variable molecular structures and tunable energy levels, enables a large material pool for realizing the potential of multicomponent BHJ solar cells [2329]. Li et al. [30] earlier reported an NFA-based binary system BDB-T:ITIC mixed with binary fullerenes as acceptor additives. Consequently, the optical band gaps of the NFA-blended films were reduced and the carrier transport processes were enhanced. As a result, the open-circuit voltage (VOC), the short-circuit current-density (JSC), and the fill factor (FF) were simultaneously improved, promoting an ultimate PCE up to 12.8%. Bi et al.[31] developed an individual nanostructure optimized quaternary system based on two donors and two acceptors. High crystallinity DR3TBDTT was dispersed in PTB7-Th to enhance the domain purity, while PC71BM was used as phase modifier to promote favorable FOIC packing. Thus, the nanoscale morphologies of the donors and the acceptors were optimized individually, which helped to increase carrier mobilities and suppress monomolecular recombination, thereby contributing to a champion PCE of 13.51%. Recent work from Ma et al. [32] proposed an efficient quaternary system combining a basic binary blend including fullerene and NFA. The third component, Br-ITIC, was added to maximize the photon harvesting, and PC71BM was used as the fourth component to optimize the molecular arrangement and phase separation of the active layer, leading to a PCE of 16.8%. Therefore, multicomponent blending is an effective strategy to promote the PCEs of OSCs. However, quaternary or ternary blending has rarely been applied in large-area photovoltaic modules.

    In this work, a quaternary blending strategy was used in the fabrication of small-area photovoltaic devices and large-area photovoltaic modules. We have explored a quaternary system, including one polymer donor PM6, one fullerene acceptor PC71BM, and two NFAs Y6 and ITIC. The PC71BM was added as the third component in the PM6:Y6 system to optimize the charge transport. The ITIC was further added as the fourth component to maximize the photon harvesting. As a result, a champion PCE of 16.71% was achieved in the quaternary device after an optimization of photovoltaic parameters. Furthermore, a certified PCE of 12.36% was achieved for the large-area (19.34  cm2) module, which is one of the highest efficiencies for inverted organic solar modules to date. The excellent photovoltaic performance demonstrates the great potential of using multicomponent organic solar modules for practical applications.

    2. EXPERIMENT

    A. Materials

    The PM6, Y6, ITIC, and PC71BM were purchased from Solarmer Materials Inc. The ZnO precursor solution was prepared by dissolving zinc acetate dehydrate and ethanolamine in the solution of 2-methoxyethanol with a concentration of 0.5 mol/L.

    B. Device Fabrication

    The multiple OSCs were constructed with indium tin oxide (ITO)/ZnO/active layer/MoOx/Ag. For small-area device fabrication, the ZnO precursor solution was spin-coated on the oxygen plasma-pretreated ITO at 3000 r/min and baked at 200°C for 1 h in air. PM6, Y6, ITIC, and PC71BM were dissolved in chloroform with different mass ratios. The mass concentration of the polymer was kept at 7  g/L. Chloronaphthalene (0.8%) was added to optimize the phase separation. The blend solutions were then spin-coated onto the ZnO layer at an optimized speed of 2400 r/min, obtaining the thickness of 100  nm, and were subsequently annealed at 50°C for 10 min. Finally, a 10 nm thick MoOx layer was deposited as the anode interlayer by thermal evaporation under less than 5×105  Pa, followed by deposition of 80 nm of Ag as the top electrode.

    For large-area module fabrication, the modules were fabricated with a similar architecture to the small-area OSCs. The patterned ITO-coated glass substrates (6  cm×6  cm with P1 scribe) were spin-coated with a ZnO precursor solution at 3000 r/min and baked at 200°C for 1 h in air. The quaternary blend solution (PM6:Y6:ITIC:PC71BM=1:1.15:0.05:0.2) was prepared with a polymer weight concentration of 9  g/L. Chloronaphthalene (0.8%) was added as additive. The quaternary solution was spin-coated on the ZnO layer at 5000 r/min in N2 atmosphere, and the films were subsequently thermally annealed at 50°C for 10 min. Then a 10 nm thick MoOx layer was deposited as the anode interlayer by thermal evaporation under less than 5×105  Pa. Finally, 80 nm of Ag was thermally evaporated under less than 5×105  Pa. The series connection is realized with the typical P1-P3 laser (532 nm, 10 ns) patterning method, as shown later in this paper, and the geometrical filling factor is 95.5%.

    C. Characterization

    The density-voltage (J-V) curves were measured by a Keithley 2400 source meter under AM 1.5 G light (100  mWcm2) from an SAN-EI electric solar simulator. The light intensity was calibrated using a standard silicon solar cell. The typical small-device area of 0.063  cm2 is defined by a shadow mask. For the large-area module, the total illumination area is 19.34  cm2, and the external quantum efficiency (EQE) was recorded by QE-R from Enli Technology. The UV-vis absorption spectra were measured by a Agilent Carry 5000 UV-vis spectrometer. Atomic force microscopy (AFM) images of the sample surfaces were obtained on a Cypher S atomic force microscope.

    3. RESULTS AND DISCUSSION

    (a) Chemical structures and (b) normalized absorption spectra of PM6, Y6, ITIC, and PC71BM. (c) J-V curves and (d) EQE spectra of the multiple OSCs.

    Figure 1.(a) Chemical structures and (b) normalized absorption spectra of PM6, Y6, ITIC, and PC71BM. (c) J-V curves and (d) EQE spectra of the multiple OSCs.

    AFM height images and Rq values of the multiple OSCs. PM6:Y6:ITIC:PC71BM equals (a) 1:1.4:0:0, (b) 1:1.2:0:0.2, (c) 1:1.15:0.05:0.2, (d) 1:1.1:0.1:0.2, (e) 1:0.6:0.6:0.2, and (f) 1:0:1.2:0.2.

    Figure 2.AFM height images and Rq values of the multiple OSCs. PM6:Y6:ITIC:PC71BM equals (a) 1:1.4:0:0, (b) 1:1.2:0:0.2, (c) 1:1.15:0.05:0.2, (d) 1:1.1:0.1:0.2, (e) 1:0.6:0.6:0.2, and (f) 1:0:1.2:0.2.

    Jph−Veff curves of the multiple OSCs.

    Figure 3.JphVeff curves of the multiple OSCs.

    (a) Device architecture, (b) realistic image, and (c) J-V curve of the large-area organic photovoltaic module. (d) The cellphone charged by the large-area organic photovoltaic module (see Visualization 1).

    Figure 4.(a) Device architecture, (b) realistic image, and (c) J-V curve of the large-area organic photovoltaic module. (d) The cellphone charged by the large-area organic photovoltaic module (see Visualization 1).

    Independent certification result of the large-area module based on the PM6:Y6:ITIC:PC71BM (1:1.15:0.05:0.2) device from the Shanghai Institute of Microsystem and Information Technology, Chinese Academy of Sciences, confirming a high PCE of 12.36% (Certificate No. 19TR120402) (area=19.34 cm2).

    Figure 5.Independent certification result of the large-area module based on the PM6:Y6:ITIC:PC71BM (1:1.15:0.05:0.2) device from the Shanghai Institute of Microsystem and Information Technology, Chinese Academy of Sciences, confirming a high PCE of 12.36% (Certificate No. 19TR120402) (area=19.34  cm2).

    4. CONCLUSION

    In summary, we successfully fabricated a series of high-performance multiple OSCs. Fullerene and NFA (namely, PC71BM and ITIC) were sequentially added to the binary system to optimize the photovoltaic properties of the multiple blend films. With the strategy of integrating the advantages of multiple components, an optimized PCE up to 16.71% was obtained. Based on the exploration of quaternary devices, a large-area photovoltaic module was manufactured with a PCE of 13.25% (certified as 12.36%). The excellent performance of photovoltaic devices and large-area modules proves the synergy of multiple components, paving a way to the commercial application of the high-performance photovoltaic cells.

    APPENDIX A

    The main text presents the photovoltaic parameters of the large-area module measured in house. Here shows the independent certification result of the large-area module (Fig.?5). A certified PCE of 12.36% was obtained.

    References

    [1] G. Yu, J. Gao, J. C. Hummelen, F. Wudl, A. J. Heeger. Polymer photovoltaic cells: enhanced efficiencies via a network of internal donor-acceptor heterojunctions. Science, 270, 1789-1791(1995).

    [2] D. M. Guldi, B. M. Illescas, C. M. Atienza, M. Wielopolski, N. Martin. Fullerene for organic electronics. Chem. Soc. Rev., 38, 1587-1597(2009).

    [3] Q. Wei, T. Nishizawa, K. Tajima, K. Hashimoto. Self-organized buffer layers in organic solar cells. Adv. Mater., 20, 2211-2216(2008).

    [4] P. P. Khlyabich, B. Burkhart, B. C. Thompson. Efficient ternary blend bulk heterojunction solar cells with tunable open-circuit voltage. J. Am. Chem. Soc., 133, 14534-14537(2011).

    [5] K. Vandewal, K. Tvingstedt, A. Gadisa, O. Inganas, J. V. Manca. On the origin of the open-circuit voltage of polymer-fullerene solar cells. Nat. Mater., 8, 904-909(2009).

    [6] J. Benduhn, K. Tvingstedt, F. Piersimoni, S. Ullbrich, Y. Fan, M. Tropiano, K. A. McGarry, O. Zeika, M. K. Riede, C. J. Douglas, S. Barlow, S. R. Marder, D. Neher, D. Spoltore, K. Vandewal. Intrinsic non-radiative voltage losses in fullerene-based organic solar cells. Nat. Energy, 2, 17053(2017).

    [7] B. Fan, X. Du, F. Liu, W. Zhong, L. Ying, R. Xie, X. Tang, K. An, J. Xin, N. Li, W. Ma, C. J. Brabec, F. Huang, Y. Cao. Fine-tuning of the chemical structure of photoactive materials for highly efficient organic photovoltaics. Nat. Energy, 3, 1051-1058(2018).

    [8] J. Yuan, Y. Zhang, L. Zhou, G. Zhang, H.-L. Yip, T.-K. Lau, X. Lu, C. Zhu, H. Peng, P. A. Johnson, M. Leclerc, Y. Cao, J. Ulanski, Y. Li, Y. Zou. Single-junction organic solar cell with over 15% efficiency using fused-ring acceptor with electron-deficient core. Joule, 3, 1140-1151(2019).

    [9] K. Jiang, Q. Wei, J. Y. L. Lai, Z. Peng, H. K. Kim, J. Yuan, L. Ye, H. Ade, Y. Zou, H. Yan. Alkyl chain tuning of small molecule acceptors for efficient organic solar cells. Joule, 3, 3020-3033(2019).

    [10] L. Hong, H. Yao, Z. Wu, Y. Cui, T. Zhang, Y. Xu, R. Yu, Q. Liao, B. Gao, K. Xian, H. Y. Woo, Z. Ge, J. Hou. Eco-compatible solvent-processed organic photovoltaic cells with over 16% efficiency. Adv. Mater., 31, 1903441(2019).

    [11] Y. Cui, H. Yao, J. Zhang, K. Xian, T. Zhang, L. Hong, Y. Wang, Y. Xu, K. Ma, C. An, C. He, Z. Wei, F. Gao, J. Hou. Single-junction organic photovoltaic cells with approaching 18% efficiency. Adv. Mater., 32, 1908205(2020).

    [12] Z. Jia, Z. Chen, X. Chen, L. Bai, H. Zhu, Y. M. Yang. Understanding of the nearly linear tunable open-circuit voltages in ternary organic solar cells based on two non-fullerene acceptors. J. Phys. Chem. Lett., 12, 151-156(2020).

    [13] Q. Liu, Y. Jiang, K. Jin, J. Qin, J. Xu, W. Li, J. Xiong, J. Liu, Z. Xiao, K. Sun, S. Yang, X. Zhang, L. Ding. 18% efficiency organic solar cells. Sci. Bull., 65, 272-275(2020).

    [14] J. Yao, B. Qiu, Z. G. Zhang, L. Xue, R. Wang, C. Zhang, S. Chen, Q. Zhou, C. Sun, C. Yang, M. Xiao, L. Meng, Y. Li. Cathode engineering with perylene-diimide interlayer enabling over 17% efficiency single-junction organic solar cells. Nat. Commun., 11, 2726(2020).

    [15] Z. Luo, R. Ma, T. Liu, J. Yu, Y. Xiao, R. Sun, G. Xie, J. Yuan, Y. Chen, K. Chen, G. Chai, H. Sun, J. Min, J. Zhang, Y. Zou, C. Yang, X. Lu, F. Gao, H. Yan. Fine-tuning energy levels via asymmetric end groups enables polymer solar cells with efficiencies over 17%. Joule, 4, 1236-1247(2020).

    [16] C. Zhu, J. Yuan, F. Cai, L. Meng, H. Zhang, H. Chen, J. Li, B. Qiu, H. Peng, S. Chen, Y. Hu, C. Yang, F. Gao, Y. Zou, Y. Li. Tuning the electron-deficient core of a non-fullerene acceptor to achieve over 17% efficiency in a single-junction organic solar cell. Energy Environ. Sci., 13, 2459-2466(2020).

    [17] L. Zhan, S. Li, T.-K. Lau, Y. Cui, X. Lu, M. Shi, C.-Z. Li, H. Li, J. Hou, H. Chen. Over 17% efficiency ternary organic solar cells enabled by two non-fullerene acceptors working in an alloy-like model. Energy Environ. Sci., 13, 635-645(2020).

    [18] L. Liu, Y. Kan, K. Gao, J. Wang, M. Zhao, H. Chen, C. Zhao, T. Jiu, A. K. Jen, Y. Li. Graphdiyne derivative as multifunctional solid additive in binary organic solar cells with 17.3% efficiency and high reproductivity. Adv. Mater., 32, 1907604(2020).

    [19] T. Wang, R. Sun, M. Shi, F. Pan, Z. Hu, F. Huang, Y. Li, J. Min. Solution-processed polymer solar cells with over 17% efficiency enabled by an iridium complexation approach. Adv. Energy Mater., 10, 2000590(2020).

    [20] X. Ma, J. Wang, J. Gao, Z. Hu, C. Xu, X. Zhang, F. Zhang. Achieving 17.4% efficiency of ternary organic photovoltaics with two well-compatible nonfullerene acceptors for minimizing energy loss. Adv. Energy Mater., 10, 2001404(2020).

    [21] Q. Ma, Z. Jia, L. Meng, J. Zhang, H. Zhang, W. Huang, J. Yuan, F. Gao, Y. Wan, Z. Zhang, Y. Li. Promoting charge separation resulting in ternary organic solar cells efficiency over 17.5%. Nano Energy, 78, 105272(2020).

    [22] T. Jiang, Z. Chen, X. Chen, T. Liu, X. Chen, W. E. I. Sha, H. Zhu, Y. Yang. Realizing high efficiency over 20% of low-bandgap Pb-Sn-alloyed perovskite solar cells by in situ reduction of Sn4+. Sol. RRL, 4, 1900467(2019).

    [23] Y. Yang, W. Chen, L. Dou, W.-H. Chang, H.-S. Duan, B. Bob, G. Li, Y. Yang. High-performance multiple-donor bulk heterojunction solar cells. Nat. Photonics, 9, 190-198(2015).

    [24] J. Hou, O. Inganas, R. H. Friend, F. Gao. Organic solar cells based on non-fullerene acceptors. Nat. Mater., 17, 119-128(2018).

    [25] G. Zhang, J. Zhao, P. C. Y. Chow, K. Jiang, J. Zhang, Z. Zhu, J. Zhang, F. Huang, H. Yan. Nonfullerene acceptor molecules for bulk heterojunction organic solar cells. Chem. Rev., 118, 3447-3507(2018).

    [26] W. Huang, P. Cheng, Y. M. Yang, G. Li, Y. Yang. High-performance organic bulk-heterojunction solar cells based on multiple-donor or multiple-acceptor components. Adv. Mater., 30, 1705706(2018).

    [27] R. Yu, H. Yao, J. Hou. Recent progress in ternary organic solar cells based on nonfullerene acceptors. Adv. Energy Mater., 8, 1702814(2018).

    [28] J. Lee, S. M. Lee, S. Chen, T. Kumari, S. H. Kang, Y. Cho, C. Yang. Organic photovoltaics with multiple donor-acceptor pairs. Adv. Mater., 31, 1804762(2019).

    [29] X. Chen, Z. Jia, Z. Chen, T. Jiang, L. Bai, F. Tao, J. Chen, X. Chen, T. Liu, X. Xu, C. Yang, W. Shen, W. E. I. Sha, H. Zhu, Y. Yang. Efficient and reproducible monolithic perovskite/organic Tandem solar cells with low-loss interconnecting layers. Joule, 4, 1594-1606(2020).

    [30] W. Li, D. Yan, F. Liu, T. Russell, C. Zhan, J. Yao. High-efficiency quaternary polymer solar cells enabled with binary fullerene additives to reduce nonfullerene acceptor optical band gap and improve carriers transport. Sci. China Chem., 61, 1609-1618(2018).

    [31] Z. Bi, H. B. Naveed, X. Sui, Q. Zhu, X. Xu, L. Gou, Y. Liu, K. Zhou, L. Zhang, F. Zhang, X. Liu, W. Ma. Individual nanostructure optimization in donor and acceptor phases to achieve efficient quaternary organic solar cells. Nano Energy, 66, 104176(2019).

    [32] X. Ma, J. Wang, Q. An, J. Gao, Z. Hu, C. Xu, X. Zhang, Z. Liu, F. Zhang. Highly efficient quaternary organic photovoltaics by optimizing photogenerated exciton distribution and active layer morphology. Nano Energy, 70, 104496(2020).

    [33] R. Yu, H. Yao, Y. Cui, L. Hong, C. He, J. Hou. Improved charge transport and reduced nonradiative energy loss enable over 16% efficiency in ternary polymer solar cells. Adv. Mater., 31, 1902302(2019).

    [34] T. Yan, W. Song, J. Huang, R. Peng, L. Huang, Z. Ge. 16.67% rigid and 14.06% flexible organic solar cells enabled by ternary heterojunction strategy. Adv. Mater., 31, 1902210(2019).

    [35] J. Lee, Y. H. Seo, S. N. Kwon, D. H. Kim, S. Jang, H. Jung, Y. Lee, H. Weerasinghe, T. Kim, J. Y. Kim, D. Vak, S. I. Na. Slot-die and roll-to-roll processed single junction organic photovoltaic cells with the highest efficiency. Adv. Energy Mater., 9, 1901805(2019).

    [36] C.-Y. Liao, Y. Chen, C.-C. Lee, G. Wang, N.-W. Teng, C.-H. Lee, W.-L. Li, Y.-K. Chen, C.-H. Li, H.-L. Ho, P. H.-S. Tan, B. Wang, Y.-C. Huang, R. M. Young, M. R. Wasielewski, T. J. Marks, Y.-M. Chang, A. Facchetti. Processing strategies for an organic photovoltaic module with over 10% efficiency. Joule, 4, 189-206(2020).

    [37] X. Meng, L. Zhang, Y. Xie, X. Hu, Z. Xing, Z. Huang, C. Liu, L. Tan, W. Zhou, Y. Sun, W. Ma, Y. Chen. A general approach for lab-to-manufacturing translation on flexible organic solar cells. Adv. Mater., 31, 1903649(2019).

    [38] S. Dong, T. Jia, K. Zhang, J. Jing, F. Huang. Single-component non-halogen solvent-processed high-performance organic solar cell module with efficiency over 14%. Joule, 4, 2004-2016(2020).

    [39] R. Sun, Q. Wu, J. Guo, T. Wang, Y. Wu, B. Qiu, Z. Luo, W. Yang, Z. Hu, J. Guo, M. Shi, C. Yang, F. Huang, Y. Li, J. Min. A layer-by-layer architecture for printable organic solar cells overcoming the scaling lag of module efficiency. Joule, 4, 407-419(2020).

    Ziyan Jia, Zeng Chen, Xu Chen, Jizhong Yao, Buyi Yan, Rui Sheng, Haiming Zhu, Yang (Michael) Yang. 19.34 cm2 large-area quaternary organic photovoltaic module with 12.36% certified efficiency[J]. Photonics Research, 2021, 9(3): 324
    Download Citation