Xinyou HUANG, Yumin LIU, Yang LIU, Xiaoying LI, Yagang FENG, Xiaopu CHEN, Penghui CHEN, Xin LIU, Tengfei XIE, Jiang LI. Fabrication and Characterizations of Yb:YAG Transparent Ceramics Using Alcohol-water Co-precipitation Method [J]. Journal of Inorganic Materials, 2021, 36(2): 217
- Journal of Inorganic Materials
- Vol. 36, Issue 2, 217 (2021)
. TG-DTA curves of the as-prepared precursors synthesized with pure water (a) and alcohol-water (b) solvents
. XRD patterns of the powders calcined at 1250 ℃ for 4 h synthesized with pure water and alcohol-water solvents
. FESEM micrographs of the as-synthesized precursors synthesized with pure water (a) and alcohol-water (b) solvents
. FESEM micrographs of the 5at%Yb:YAG powders synthesized with pure water (a) and alcohol-water (b) solvents calcined at 1250 ℃ for 4 h
. Photographs (a) and in-line transmittances (b) of 5at%Yb:YAG ceramics (2.2 mm thickness) sintered at different temperatures for 20 h
. FESEM micrographs of the thermally-etched surfaces of 5at%Yb:YAG ceramics sintered at various temperatures for 20 h
. Relative densities and average grain sizes of the 5at%Yb:YAG ceramics sintered at various temperatures for 20 h
. In-line transmission curves of the 5at%Yb:YAG ceramics (2.2 mm thickness) sintered at 1800 ℃ for various holding time
. FESEM micrographs of the thermally-etched surfaces of Yb:YAG ceramics sintered at 1800 ℃ for various holding time: (a) 10 h, (b) 20 h, (c) 50 h
. Absorption and emission cross sections of the 5at%Yb:YAG ceramic sintered at 1800 ℃ for 50 h
. Gain cross sections of the 5at%Yb:YAG ceramic sintered at 1800 ℃ for 50 h
Set citation alerts for the article