• Chinese Journal of Lasers
  • Vol. 43, Issue 7, 702001 (2016)
Zhang Pan* and Wang Xuyue
Author Affiliations
  • [in Chinese]
  • show less
    DOI: 10.3788/cjl201643.0702001 Cite this Article Set citation alerts
    Zhang Pan, Wang Xuyue. Element Diffusion and Material Properties in Transition Layer of Bending Zone in Laminated Plates[J]. Chinese Journal of Lasers, 2016, 43(7): 702001 Copy Citation Text show less

    Abstract

    Laser bending experiments are performed on stainless steel-carbon steel laminated plates with thickness of 1.0, 1.5, and 2.0 mm. The element diffusion in the transition layer of the bending zone is analyzed by means of metallographic microscope, electron microprobe and energy dispersive spectrometer, the nano-indentation tests are used to obtain the nano-hardness and elastic modulus of the transition layer, and the variation in elastic modulus, nano-hardness and yield strength is analyzed eventually. The results demonstrate that the element in the transition layer diffuses continuously and steadily along the plate thickness, the diffusion ranges for Fe, Ni, and Cr are similar, and the transition layer thickness for 1.0, 1.5, and 2.0 mm thick laminated plates increases by 2.5, 3.5, and 3.0 μm, respectively. Good material properties in transition layer is ensured by element diffusion in the bending zone, and favorable metallurgical bond in laminated plates is also improved.
    Zhang Pan, Wang Xuyue. Element Diffusion and Material Properties in Transition Layer of Bending Zone in Laminated Plates[J]. Chinese Journal of Lasers, 2016, 43(7): 702001
    Download Citation