Abstract
1. Introduction
In the space radiation environment, there are many kinds of energic particles, such as protons, electrons, heavy ions. Energic particle strike may damage the electronic system, which leads to the system function failure. Nowadays, with wide applications of system on chips (SoCs) in spacecrafts and satellites, space-grade SoCs call for novel non-volatile memory devices featuring both high speed and high reliability. Magneto-resistive random access memory (MRAM) as one of the non-volatile memory devices[
It is often claimed that the MTJ is inherently immune to the total ionizing dose (TID) radiation[
In this paper, we perform Co-60 γ-ray radiation experiments on SOT magnetic film and SOT Hall devices with the same stack structure. We observe that magnetic properties of SOT film remain unchanged and even the irradiation dose accumulates to 300 krad(Si), while the anomalous Hall resistance of SOT Hall devices exhibits a reversible changing behavior during the radiation. According to the analysis of the interaction of γ-ray with magnetic materials and the Hall device, we propose a possible explanation to understand this phenomenon. Our results pave a way for further exploration of transient TID radiation effect in SOT-MTJ and will also be helpful to the radiation-hardened SOT-MRAM device design.
2. Experimental description
The stack structure of SOT magnetic film used in our experiment is Si/SiO2/Ta(5)/Pt(3)/Co(1)/Ta(5)/MgO(2) (in nanometers). It is grown by magnetron sputtering, in which the bottom Ta layer acts as the seed layer that determines the crystal orientation of the upper layer grown. The Co layer is a magnetic free layer with perpendicular anisotropy. The top Ta and MgO layer act as the capping layer for protection. Then SOT magnetic films are separated into two parts. One part of the films is cut into a 1 × 1 mm2 fragment as shown in Fig. 1(a), in order to study the influence of radiation on magnetic properties of the free layer. Another part of the films is patterned into a Hall device sized in 10 × 140 μm2 by I-line lithography for the RAHE–I measurement as shown in Figs. 1(b) and 1(c). When there is an electron current passing through the heavy metal Pt layer, a spin current will be produced in the direction perpendicular to the current and interacts with the magnetization of Co layer. If the spin current exceeds a critical value, the magnetization direction of the Co layer will be switched, that is the SOT effect. What is more, the state of Co magnetization can be read by anomalous Hall effect. Therefore, the SOT Hall device can be used to study the influence of radiation on magnetoelectric properties of the free layer in SOT-MTJ.
Figure 1.(Color online) (a) The structure of SOT magnetic film. (b) The structure of SOT Hall device. (c) The image of SOT Hall device.
TID experiments are performed on the Co-60 facility at room temperature. The dose rate is set as 50 rad (Si)/s. The RAHE–I measurements of SOT Hall devices and M–H hysteresis loop measurements of SOT magnetic films are conducted at 90, 120, and 300 krad (Si), respectively. The RAHE–I measurements are performed on a probe station with three-dimensional Helmholtz coil while M–H hysteresis loop measurements are carried out using the SQUID-VSM system. All the measurements are performed at room temperature.
3. Results and discussions
Fig. 2 shows the normalized hysteresis loops (M–H) and their differential curves of as-prepared magnetic films under different irradiation dose conditions. The field scanning range is from –1000 to +1000 Oe. The shape of the hysteresis loops and the coercive field are not affected by the radiation, which means the macro magnetism of the SOT film is immune to γ-ray irradiation even the accumulated dose is up to 300 krad (Si).
Figure 2.(Color online) (a) The normalized hysteresis loops of SOT magnetic films under different radiation doses. (b) The differential curves of SOT magnetic films hysteresis loops under different radiation doses. The magnetic field sweep rate is 15 Oe/s. All the experiments are performed at room temperature.
However, the electrical measurement results for the SOT Hall device are quite different. Fig. 3 shows the current-induced magnetization switching of SOT Hall devices, which is probed by anomalous Hall effect under in-plane magnetic field Hx of 50 Oe. It can be seen that the shape of the loops shows a reversible change during radiation. Before radiation, the switching loop of RAHE–H is normal without any disturbing. As the dose of radiation increases, the switching loops become more and more irregular. When the dose accumulates 120 krad (Si), it exhibits a parabola-like behavior, which means the anomalous Hall resistance of the SOT Hall device is affected by radiation. According to the results mentioned above, the magnetic properties of SOT film remain unchanged during radiation. Thus, we infer that there must be an altering of electronic properties in the Pt layer induced by radiation. Interestingly, the switching loop returns to normal at the dose of 300 krad (Si). This phenomenon has not been observed by any other researchers yet. Here we propose a possible explanation as discussed below.
Figure 3.(Color online) (a) The anomalous Hall curves of SOT Hall device films under different radiation doses at room temperature. (b) The differential curves of SOT Hall devices films under different radiation doses at room temperature. The in plane magnetic field is 50 Oe. The pulse time of current is 0.5 ms.
Before we launch further analysis, we need to note the fundamental of anomalous Hall effect first. Although the origin is still confused, it is generally accepted that the magnetic conductor exists in spontaneous perpendicular magnetization. The magnetization can be equivalent to magnetic field H. When the conductor carries a current (in x axis) and the effective magnetic field that is in perpendicular direction (in z axis), the carriers will deviate from their path and accumulate at the edge of the conductor by the Lorentz force, which gives a voltage in the y axis called Hall voltage[
Theoretically, Hall resistance includes normal Hall resistance and anomalous Hall resistance. Without external field, normal Hall resistance can be ignored. So the anomalous Hall resistance RAHE has the relation with the writing current as follows:
where Rs is the anomalous Hall coefficient, which only depends on the specific material characteristics, Mz is the component of magnetization perpendicular to the surface of the Hall device which can be tuned by current through SOT effect[
According to Eq. (1), RAHE is in proportion to Mz. From the results of Fig. 3, it seems like that γ-ray radiation has made some influence on the magnetization of Co layer. However, as mentioned above, the macro magnetism of the Co layer remains unchanged during the radiation as shown in Fig. 2. Thus, there must be another reason for the phenomena of Hall measurements.
Theoretically, the anomalous Hall resistance comes from the anomalous Hall voltage, which depends on the charge distribution on Hall electrodes. Hereby we infer that there may be extra radiation-induced non-equilibrium carriers that alter the anomalous Hall voltage. Generally, the non-equilibrium carriers in metal will recombine in a time of nanoseconds to microseconds. However, specific to our sample, non-equilibrium carriers induced by radiation are affected by the horizontal driving electronic field and the perpendicular effective magnetic field at the same time. Therefore, the non-equilibrium carriers will accumulate at the both edge of Hall electrodes through the Lorentz force that makes the recombination time much longer. On the other hand, it should be noted that because the positive charge and negative charge have different mobility in the metal, non-equilibrium carrier distribution at the edge of Hall electrodes is asymmetric, which contributes to an irregular anomalous Hall resistance. Thus, we introduce an extra time-dependent Hall resistance term in the Eq. (1) as the following:
where
On the one hand, the non-equilibrium anomalous Hall coefficient
Figure 4.(Color online) (a) The distribution of equilibrium carriers in the Hall device before radiation. (b) The distribution of nonequilibrium carriers induced by irradiation in the Hall device.
On the other hand, although the dose of radiation is increasing, the number of charge recombination centers is limited. They constantly capture the non-equilibrium carriers to recombination on time scales that makes the carriers intensity change to a new constant[
Therefore, according to the results mentioned above, we have reason to believe that the SOT-MTJ devices may not be as robust as STT-MTJ or Toggle-MTJ when used in the γ-ray radiation environment. Because the SOT-MTJ utilizes the SOT effect to write the data, the temporarily non-equilibrium carriers induced by radiation will lead to an inhomogeneous Hall electronic field that may have influence on the switching characteristics of the SOT-MTJ device. Fortunately, the non-equilibrium state is temporary, therefore its influence will disappear when the device relaxes to a new equilibrium state.
4. Conclusion
In summary, we make a survey on the TID effect on SOT magnetic films and Hall devices with the same stack. According to the results of our experiments, the γ-ray radiation had no effect on the magnetic properties of SOT magnetic films even though the total ionized dose reached 300 krad (Si). That means magnetic films have a robust tolerance of TID. However, we find a reversible change for the RAHE–I loop of the Hall device during radiation, which means the magnetoelectronic transport properties of carriers are affected by the radiation. We introduce an extra time and current-related term
On the other hand, for the SOT-MTJ device used in the γ-ray radiation environment, we infer that the inhomogeneous Hall electronic field generated by the non-equilibrium carriers during the radiation may have an unknown effect on the switching process of SOT-MTJ as it may break the time-reversal symmetry according to our experimental results and analysis. It means that SOT-MTJ may be not as anti-radiation as conventional MTJ. Therefore, our results are also helpful for the radiation-hardened SOT-MRAM design.
Acknowledgements
This work is financially supported by Strategic Priority Research Program of the CAS (Grant No. XDA18000000) and Youth Innovation Promotion Association of CAS (Grant No. 2015097).
References
[1] J M Hu, L Q Chen, C W Nan. Multiferroic heterostructures integrating ferroelectric and magnetic materials. Adv Mater, 28, 15(2016).
[2] N Perrissin, S Lequeux, N Strelkov et al. A highly thermally stable sub-20 nm magnetic random-access memory based on perpendicular shape anisotropy. Nanoscale, 10, 12187(2018).
[3] H Sato, S Ikeda, H Ohno. Magnetic tunnel junctions with perpendicular easy axis at junction diameter of less than 20nm. Jpn J Appl Phys, 56, 9(2017).
[4] S Gerardin, A Paccagnella. Present and future non-volatile memories for space. IEEE Trans Nucl Sci, 57, 3016(2010).
[5] Y Cui, L Yang, T Gao et al. Total ionizing radiation-induced read bit-errors in toggle magnetoresistive random-access memory devices. Chin Phys B, 26, 087501(2017).
[6] S I R Arias, D R Muñoz, S Cardoso et al. Total ionizing dose (TID) evaluation of magnetic tunnel junction (MTJ) current sensors. Sens Actuators A, 225, 119(2015).
[7] K Garello, C O Avci, I M Miron et al. Ultrafast magnetization switching by spin-orbit torques. Appl Phys Lett, 105, 5(2014).
[8] L Q Liu, O J Lee, T J Gudmundsen et al. Current-induced switching of perpendicularly magnetized magnetic layers using spin torque from the spin Hall effect. Phys Rev Lett, 109, 5(2012).
[9] N Sato, A El-Ghazaly, R M White et al. Effect of Mg oxidation degree on Rashba-effect-induced torques in Ta/CoFeB/Mg(MgO) multilayer. IEEE Trans Magn, 52, 4(2016).
[10] H X Wei, Q H Qin, M Ma et al. 80% tunneling magnetoresistance at room temperature for thin Al-O barrier magnetic tunnel junction with CoFeB as free and reference layers. J Appl Phys, 101, 3(2007).
[11] G Q Yu, P Upadhyaya, Y B Fan et al. Switching of perpendicular magnetization by spin-orbit torques in the absence of external magnetic fields. Nat Nanotechnol, 9, 548(2014).
[12]
[13]
[14] B Wang, Z Wang, C Hu et al. Radiation-hardening techniques forspin orbit torque-MRAM peripheral circuitry. IEEE Trans Magn, 54, 1(2018).
[15]
[16] E H Hall. On a new action of the magnet on electric currents. Am J Math, 2, 287(1879).
[17] N Nagaosa, J Sinova, S Onoda et al. Anomalous Hall effect. Rev Mod Phys, 82, 1539(2010).
[18] J Smit. The spontaneous Hall effect in ferromagnetics I. Physica, 21, 877(1955).
[19] J Smit. The spontaneous Hall effect in ferromagnetics II. Physica, 24, 39(1958).
[20] L Berger. Side-jump mechanism for the Hall effect of ferromagnets. Phys Rev B, 2, 4559(1970).
[21] W Kong, C Wan, X Wang et al. Spin–orbit torque switching in a T-type magnetic configuration with current orthogonal to easy axes. Nat Commun, 10, 1(2019).
[22]
Set citation alerts for the article
Please enter your email address