TiAl alloy has excellent properties of low density and high specific strength, which is a potential structural material for aero-engine. The service temperature of TiAl alloy is limited in the range of 700-900 ℃, which is further improved by preparation of high temperature thermal protection coating. In the present work, a new type of TiAlCrY/YSZ coating was prepared on the TiAl alloy by plasma spray technologies, of which long-term service performance at high temperature was compared with the traditional NiCrAlY/YSZ coating. It was found that the TiAlCrY/YSZ coating remained intact after served 300 h at 1100 ℃ in the air, showing excellent high temperature performance, while the service lifetime of the NiCrAlY/YSZ coating at 1100 ℃ was less than 100 h. The microstructure observation found that a continuous and dense TGO composed of Al₂O₃ was continuously formed on the TiAlCrY bonding coating, suggesting that TiAlCrY coating has good interfacial compatibility with the YSZ top coating. Moreover, the thickness of TGO was still less than 8 μm after served 300 h at 1100 ℃ in the air. As compared with traditional NiCrAlY/YSZ coating, the TiAlCrY/YSZ coating is a more suitable high temperature thermal coating ever for TiAl alloys.