• Photonics Research
  • Vol. 8, Issue 11, 1671 (2020)
Shengnan Zhang, Jianli Zhang*, Jiangdong Gao, Xiaolan Wang, Changda Zheng, Meng Zhang, Xiaoming Wu, Longquan Xu, Jie Ding, Zhijue Quan, and Fengyi Jiang
Author Affiliations
  • National Institute of LED on Silicon Substrate, Nanchang University, Nanchang 330096, China
  • show less
    DOI: 10.1364/PRJ.402555 Cite this Article Set citation alerts
    Shengnan Zhang, Jianli Zhang, Jiangdong Gao, Xiaolan Wang, Changda Zheng, Meng Zhang, Xiaoming Wu, Longquan Xu, Jie Ding, Zhijue Quan, Fengyi Jiang, "Efficient emission of InGaN-based light-emitting diodes: toward orange and red," Photonics Res. 8, 1671 (2020) Copy Citation Text show less

    Abstract

    Indium gallium nitride (InGaN)-based light-emitting diodes (LEDs) are considered a promising candidate for red-green-blue (RGB) micro displays. Currently, the blue and green LEDs are efficient, while the red ones are inefficient for such applications. This paper reports our work of creating efficient InGaN-based orange and red LEDs on silicon(111) substrates at low current density. Based on the structure of InGaN yellow LEDs, by simply reducing the growth temperature of all the yellow quantum wells (QWs), we obtained 599 nm orange LEDs with peak wall-plug efficiency (WPE) of 18.1% at 2 A/cm2. An optimized QW structure was proposed that changed two of the nine yellow QWs to orange ones. Compared with the sample containing nine orange QWs, the sample with two orange QWs and seven yellow QWs showed similar emission spectra but a much higher peak WPE up to 24.0% at 0.8 A/cm2 with a wavelength of 608 nm. The improvement of peak WPE can be attributed to the improved QW quality and the reduced active recombination volume. Subsequently, a series of efficient InGaN-based orange and red LEDs was demonstrated. With further development, the InGaN-based red LEDs are believed to be attainable and can be used in micro LED displays.

    1. INTRODUCTION

    Red-green-blue (RGB) micro light-emitting diode (LED) displays and related applications are attracting extensive attention in recent years because of their outstanding features [14]. Besides the difficulty in transferring massive LED chips to the matrix, it is also a great challenge to fabricate efficient red LED chips in micro size. Currently, most commercial red LED chips are made of normal-sized aluminium gallium indium phosphide (AlGaInP) material with efficiency above 50%. But when the chip is reduced to micro size, the efficiency drops down dramatically as it has high surface recombination due to the high minority carrier diffusion length [57]. Moreover, the AlGaInP material has poor mechanical properties [8], low thermal stability [9,10], and incompatible geometry if it is integrated with InGaN-based blue and green LEDs in one pixel. Fortunately, we have the InGaN material, which theoretically can emit visible light of any wavelength. Meanwhile, the InGaN material has high thermal stability, excellent mechanical and chemical properties, and does not pose harm to the environment compared with arsenide or phosphide [11,12]. More importantly, the size effect of InGaN was reported to not be as substantial as that of AlGaInP [1315]. Thus, InGaN could be a promising material for micro red LED if the efficiency can be raised to an acceptable level.

    It is known that the efficiency of InGaN-based LEDs decreases rapidly with increasing wavelength, which is probably due to the increase in indium content in the multi-quantum wells (MQWs). A QW with longer wavelength requires higher indium content and lower growth temperature, which forms more dislocations, point defects, and severe phase separation, and ultimately leads to an increase in non-radiative recombination and lower efficiency [16,17]. The blue and green InGaN-based LEDs are very efficient to date. The typical value of peak wall-plug efficiency (WPE) is 78% for 448 nm blue at 3.5  A/cm2 [18] and 56% for 534 nm green at 1  A/cm2 [19]. However, the WPE of InGaN-based orange or red LEDs is below 2.5% [2026].

    By improving the material quality, reducing the compressive strain of InGaN QWs, and enhancing hole injection by three-dimensional (3D) p-n junctions with V-pits, we have successfully pushed the peak WPE of 574 nm yellow LEDs to 33% at 3  A/cm2 [27]. It is expected to have a good result if we apply the InGaN-based yellow LED technology to orange and red ones. In this paper, based on our previous work on InGaN-based yellow LEDs [27], we attempted to extend the efficient emission of InGaN QWs from yellow to orange and red; as a result, a significant advancement was made.

    2. METHODS AND RESULTS

    The InGaN-based orange LED films were grown on patterned silicon(111) substrates by a self-designed, metal-organic, chemical vapor deposition reactor [28]. The epi-structure was similar to that of the yellow LED reported previously [27], which consisted of a 2.8 μm n-GaN layer, 32 periods of 5 nm In0.1Ga0.9N/2  nm-GaN superlattices, nine periods of 2.5 nm In0.4Ga0.6N/13.5  nm GaN orange MQWs, a 10 nm p-Al0.2Ga0.8N electron block layer (EBL), and a 130 nm p-GaN layer. Compared with the yellow LEDs, the only change in material growth was to reduce the growth temperature of yellow QWs from 780°C to 760°C for orange LEDs. The schematic structure is illustrated in Fig. 1(a).

    Schematic epi-structures of InGaN-based orange LEDs on silicon(111) substrates: (a) Sample A with nine orange QWs and (b) Sample B with two orange QWs and seven yellow QWs. (c) TEM image of a cross section near the active region of Sample B. For easier presentation, the full thicknesses of n-GaN and p-GaN are not shown.

    Figure 1.Schematic epi-structures of InGaN-based orange LEDs on silicon(111) substrates: (a) Sample A with nine orange QWs and (b) Sample B with two orange QWs and seven yellow QWs. (c) TEM image of a cross section near the active region of Sample B. For easier presentation, the full thicknesses of n-GaN and p-GaN are not shown.

    To emphasize the importance of V-pit in InGaN-based LEDs, especially for long wavelength emission, a V-pit is added in the drawing of the structure. Besides the benefits of “3D p-n junction” to screen dislocations and enhance hole injection [2933], we find that V-pits are also helpful to the growth of orange QWs. The voids of V-pits in the bulk can reduce compressive strain, which is very crucial to growing InGaN QWs with high indium content. From the aspect of obtaining high efficiency, the density and the size of V-pits must be controlled. For V-pit density, if it is too high, too many dislocations will lower the efficiency; if it is too low, the hole injection path will become too long. For V-pit size, if it is too small, it will affect the dislocation screening results; if it is too large, it will reduce the effective volume of MQWs. According to our experiments, the optimized density and average size of V-pits are 109 cm−2 and 150 nm, respectively.

    Even though material growth was based on the optimized methods of yellow QWs, it was still very hard to grow high-quality InGaN orange QWs. The QW quality is not only determined by the indium content of each QW, but also by the accumulated indium amount of all the QWs. With such a high indium content and so many periods, the material quality of the active region is presumed to be worsened with the growth of more orange QWs. An optimized LED structure was proposed, as illustrated in Fig. 1(b). Instead of changing all the yellow QWs to orange ones, only two (QW7 and QW8) of the nine yellow QWs were changed to orange ones. The first six yellow QWs (QW1 to QW6) can act as a buffer to improve the crystal quality of the two orange QWs. The last yellow QW (QW9) can protect the two orange QWs from being damaged by high temperature during the subsequent p-GaN growth. The transmission electron microscope (TEM) image of the MQWs presented in Fig. 1(c) shows very abrupt interfaces, indicating good QW quality for Sample B. With the help of V-pits, the holes can flow easily into the two orange QWs because it has a narrower bandgap with lower energy potential. Thus, the dominant emission is expected to be from the two orange QWs when the current density is low [28,29,32]. Less active QWs mean less active recombination volume. Reducing the active recombination volume can help to shift the efficiency peak toward lower current density; this is consistent with the demand of micro LED applications which often work at low current densities.

    The two LED samples, denoted as Sample A and Sample B, were fabricated into LED chips with a size of 1  mm×1  mm and a roughened top surface and silver (Ag) reflector-coated backside via the reported film transferring technique [27,34,35]. A direct current power supply (Keithley 2635) and a spectrometer (Instrument Systems CAS140CT) equipped with an integrating sphere (Instrument Systems ISP250-211) were used for electroluminescence (EL) tests. A light source (Nikon Intensilight C-HGFI) was used for fluorescence luminescence (FL) tests.

    Figures 2(a) and 2(b) show the room temperature EL spectra of Sample A and Sample B, respectively. It is observed that the emission spectra of the two samples are similar within a low current density range from 0.4 to 10  A/cm2. It is inferred that the two orange QWs in Sample B are the main emission region at low current densities, and the remaining seven yellow QWs in Sample B do not contribute much to the emission, which is consistent with our expectations. Both samples have a large wavelength shift around 30 nm from 0.4  A/cm2 to 10  A/cm2, which is much larger than that of yellow(15  nm), green (10  nm), and blue (3  nm) LEDs, indicating stronger quantum confinement Stark effects (QCSE) in orange QWs.

    Room temperature electroluminescence spectra of (a) Sample A and (b) Sample B, where lines 1 to 9 correspond to a current density of 0.4, 0.8, 1.5, 2.0, 3.0, 4.0, 5.5, 7.5, and 10.0 A/cm2, respectively.

    Figure 2.Room temperature electroluminescence spectra of (a) Sample A and (b) Sample B, where lines 1 to 9 correspond to a current density of 0.4, 0.8, 1.5, 2.0, 3.0, 4.0, 5.5, 7.5, and 10.0  A/cm2, respectively.

    The WPE of the two samples at different current densities is plotted in Fig. 3(a). For Sample A, it has a peak WPE of 18.1% at 2  A/cm2 with a wavelength of 599 nm. Though the result is a record for an InGaN-based orange LED, it still does not meet our expectation if we compare it with the peak WPE of the yellow LED in Ref. [27] (33% @ 2  A/cm2, 574 nm) and in our recent work (42.8% @ 1  A/cm2, 577 nm) [36]. The dramatic reduction of peak WPE can be mainly attributed to the deterioration of QW quality as a result of increased indium content in the orange QWs.

    (a) Room temperature dependence of WPE on the current density of InGaN-based orange LEDs on silicon(111) substrates. Emission photos of (b) Sample B and (c) Sample A driven at a current density of 0.8 A/cm2.

    Figure 3.(a) Room temperature dependence of WPE on the current density of InGaN-based orange LEDs on silicon(111) substrates. Emission photos of (b) Sample B and (c) Sample A driven at a current density of 0.8  A/cm2.

    With a reduced number of orange QWs, Sample B has a much higher efficiency than Sample A, especially at low current densities. The peak WPE of Sample A is increased to 24.0%, where the current density is 0.8  A/cm2 and the wavelength is 608 nm. Compared with the WPE of Sample A (16.0%) at the same current density and with the same wavelength of 608 nm, a 50% improvement is made for Sample B. The luminescence images of the two samples driven at 0.8  A/cm2 are presented in Figs. 3(b) and 3(c). One can find that Sample B is much brighter.

    Generally, an increase in peak efficiency means an improvement in the quality of the QWs [37]. When comparing the FL images, Sample A shows a non-uniform red emission with many dark regions in Fig. 4(a), while Sample B shows a much more uniform red emission in Fig. 4(b). Such dark spots presented in FL images are often due to the phase separation of the In-content in MQWs of InGaN-based LEDs [19,24,38,39]. Thus, the results suggest that the high In-content phase separation problem in the orange QWs has been suppressed by reducing the number of orange QWs in Sample B, and the quality of the orange QWs has been greatly improved.

    Fluorescence luminescence images of InGaN-based orange LEDs on silicon(111) substrates, (a) Sample A and (b) Sample B, under an excited lamp source with a wavelength range from 510 to 560 nm.

    Figure 4.Fluorescence luminescence images of InGaN-based orange LEDs on silicon(111) substrates, (a) Sample A and (b) Sample B, under an excited lamp source with a wavelength range from 510 to 560 nm.

    The efficiency depends closely on the carrier recombination which is influenced by a change in the structure [40]. It is known that the energy gap of an orange QW is narrower than that of a yellow QW. With the help of V-pits for hole injection, most carrier recombination is believed to have occurred in the orange QWs at low current densities, and the active recombination volume is reduced in Sample B. It is known that current and active recombination volume can be expressed as follows: where j is the current density, q is the elementary charge, V is the active recombination volume, SE is the current injected area, RRAD is the radiative recombination rate, and RNR is the non-radiative recombination rate. As a result, for Sample B, the radiative recombination rate in the orange QWs can be greatly enhanced due to the suppressed non-radiative recombination caused by the quality improvement of the orange QWs and the decrease in active recombination volume (when the driven current density is the same). Therefore, the WPE of Sample B is much higher than that of Sample A at low current densities.

    Adopting the structure of Sample B, a series of InGaN-based LEDs with various wavelengths ranging from orange to red were successfully developed on silicon(111) substrates. All the samples have the same structure as Sample B, and the only change was to adjust the growth temperature of QW7 and QW8.

    The dependence of room temperature EL properties including WPE, full width at half-maximum (FWHM) of the emission spectrum, and the voltage on the peak wavelength are plotted in Fig. 5. All the devices are measured at 0.8  A/cm2. The WPE of the InGaN-based LEDs is 30.1% at 594 nm and drops down to 16.8% at 621 nm, which has a similar trend and decreasing slope compared with that of yellow LEDs [26]. The FWHM increases from 41.2 to 47.4 nm as the peak wavelength increases from 594 to 621 nm, which is a bit large for a micro display. Further optimization might be able to reduce it to less than 40 nm. The voltage has a negative relationship with wavelength, where the values are 2.02 V at 594 nm and 1.96 V at 621 nm. It is interesting to note that the voltage drop is lower than the average energy of emitted photons for all the samples; the extra energy is probably coming from the thermal energy carried by the carriers.

    Dependence of (a) WPE, (b) FWHM, and (c) voltage on the peak wavelength of InGaN-based orange and red LEDs at room temperature and at a current density of 0.8 A/cm2.

    Figure 5.Dependence of (a) WPE, (b) FWHM, and (c) voltage on the peak wavelength of InGaN-based orange and red LEDs at room temperature and at a current density of 0.8  A/cm2.

    It should be pointed out that the LED chips in this paper are of normal size (1  mm×1  mm), which is much larger than that of micro LEDs. Our micro LED chip technology is still under development.

    3. CONCLUSIONS

    In conclusion, we conducted research on InGaN-based orange and red LEDs based upon the structure of InGaN-based yellow LEDs. Instead of changing all the yellow QWs to orange ones, we proposed an optimized QW structure that only changes two of the nine yellow QWs to orange ones. The LED with the optimized structure was found to be much more efficient, and it achieved a record high WPE of 24.0% with a peak wavelength of 608 nm at 0.8  A/cm2. The enhanced efficiency is attributed to the improved quality of the orange QWs and the decreased active recombination volume. Based on the optimized QW structure, a series of efficient InGaN-based orange and red LEDs, with peak wavelengths from 594 nm to 621 nm and corresponding WPE from 30.1% to 16.8% at 0.8  A/cm2, were successfully developed. The results show that the material quality of InGaN-based red LEDs is very close to meeting the demands of micro display. With the development of micro LED chip technology and a further improvement in material growth, it is believed that InGaN-based red LEDs for micro display are feasible in the near future.

    References

    [1] H. Y. Lan, I. C. Tseng, Y. H. Lin, G. R. Lin, D. W. Huang, C. H. Wu. High-speed integrated micro-LED array for visible light communication. Opt. Lett., 45, 2203-2206(2020).

    [2] J. Y. Lin, H. X. Jiang. Development of microLED. Appl. Phys. Lett., 116, 100502(2020).

    [3] M. S. Wong, S. Nakamura, S. P. DenBaars. Review—progress in high performance III-nitride micro-light-emitting diodes. ECS J. Solid State Sci. Technol., 9, 015012(2020).

    [4] T. Wu, C. W. Sher, Y. Lin, C. F. Lee, S. Liang, Y. Lu, S. W. Huang Chen, W. Guo, H. C. Kuo, Z. Chen. Mini-LED and micro-LED: promising candidates for the next generation display technology. Appl. Sci., 8, 1557(2018).

    [5] K. A. Bulashevich, S. Y. Karpov. Impact of surface recombination on efficiency of III-nitride light-emitting diodes. Phys. Status Solidi (RRL), 10, 480-484(2016).

    [6] P. Royo, R. P. Stanley, M. Ilegems, K. Streubel, K. H. Gulden. Experimental determination of the internal quantum efficiency of AlGaInP microcavity light-emitting diodes. J. Appl. Phys., 91, 2563-2568(2002).

    [7] M. Boroditsky, I. Gontijo, M. Jackson, R. Vrijen, E. Yablonovitch, T. Krauss, C. C. Cheng, A. Scherer, R. Bhat, M. Krames. Surface recombination measurements on III–V candidate materials for nanostructure light-emitting diodes. J. Appl. Phys., 87, 3497-3504(2000).

    [8] S. Adachi, P. Capper, S. Kasap, A. Willoughby. Elastic properties. Properties of Group‐IV, III‐V and II‐VI Semiconductors, 41-72(2005).

    [9] M. Pattison, M. Hansen, N. Bardsley, C. Elliott, K. Lee, L. Pattison, J. Tsao. 2019 solid-state lighting R&D opportunities. DOE BTO SSL Program, 1-120(2020).

    [10] P. Dalapati, N. B. Manik, A. N. Basu. Influence of temperature on the performance of high power AlGaInP based red light emitting diode. Opt. Quantum Electron., 47, 1227-1238(2015).

    [11] B. Damilano, B. Gil. Yellow-red emission from (Ga, In)N heterostructures. J. Phys. D, 48, 403001(2015).

    [12] K. Ohkawa, T. Watanabe, M. Sakamoto, A. Hirako, M. Deura. 740-nm emission from InGaN-based LEDs on c-plane sapphire substrates by MOVPE. J. Cryst. Growth, 343, 13-16(2012).

    [13] M. S. Wong, C. Lee, D. J. Myers, D. Hwang, J. A. Kearns, T. Li, J. S. Speck, S. Nakamura, S. P. DenBaars. Size-independent peak efficiency of III-nitride micro-light-emitting-diodes using chemical treatment and sidewall passivation. Appl. Phys. Express, 12, 097004(2019).

    [14] J. T. Oh, S. Y. Lee, Y. T. Moon, J. H. Moon, S. Park, K. Y. Hong, K. Y. Song, C. Oh, J. I. Shim, H. H. Jeong, J. O. Song, H. Amano, T. Y. Seong. Light output performance of red AlGaInP-based light emitting diodes with different chip geometries and structures. Opt. Express, 26, 11194-11200(2018).

    [15] D. Hwang, A. Mughal, C. D. Pynn, S. Nakamura, S. P. DenBaars. Sustained high external quantum efficiency in ultrasmall blue III-nitride micro-LEDs. Appl. Phys. Express, 10, 032101(2017).

    [16] A. David, N. G. Young, C. A. Hurni, M. D. Craven. Quantum efficiency of III-nitride emitters: evidence for defect-assisted nonradiative recombination and its effect on the green gap. Phys. Rev. Appl., 11, 031001(2019).

    [17] W. Liu, D. Zhao, D. Jiang, P. Chen, Z. Liu, J. Zhu, X. Li, F. Liang, J. Liu, L. Zhang, H. Yang, Y. Zhang, G. Du. Shockley-Read-Hall recombination and efficiency droop in InGaN/GaN multiple-quantum-well green light-emitting diodes. J. Phys. D, 49, 145104(2016).

    [18] L. Y. Kuritzky, A. C. Espenlaub, B. P. Yonkee, C. D. Pynn, S. P. DenBaars, S. Nakamura, C. Weisbuch, J. S. Speck. High wall-plug efficiency blue III-nitride LEDs designed for low current density operation. Opt. Express, 25, 30696-30707(2017).

    [19] Q. Lv, J. Liu, C. Mo, J. Zhang, X. Wu, Q. Wu, F. Jiang. Realization of highly efficient InGaN Green LEDs with sandwich-like multiple quantum well structure: role of enhanced interwell carrier transport. ACS Photon., 6, 130-138(2019).

    [20] Z. Zhuang, D. Iida, P. Kirilenko, M. Velazquez-Rizo, K. Ohkawa. Optimal ITO transparent conductive layers for InGaN-based amber/red light-emitting diodes. Opt. Express, 28, 12311-12321(2020).

    [21] D. Iida, Z. Zhuang, P. Kirilenko, M. Velazquez-Rizo, K. Ohkawa. Demonstration of low forward voltage InGaN-based red LEDs. Appl. Phys. Express, 13, 031001(2020).

    [22] K. Ohkawa, F. Ichinohe, T. Watanabe, K. Nakamura, D. Iida. Metalorganic vapor-phase epitaxial growth simulation to realize high-quality and high-In-content InGaN alloys. J. Cryst. Growth, 512, 69-73(2019).

    [23] D. Iida, K. Niwa, S. Kamiyama, K. Ohkawa. Demonstration of InGaN-based orange LEDs with hybrid multiple-quantum-wells structure. Appl. Phys. Express, 9, 111003(2016).

    [24] J. I. Hwang, R. Hashimoto, S. Saito, S. Nunoue. Development of InGaN-based red LED grown on (0001) polar surface. Appl. Phys. Express, 7, 071003(2014).

    [25] M. Funato, M. Ueda, Y. Kawakami, Y. Narukawa, T. Kosugi, M. Takahashi, T. Mukai. Blue, green, and amber InGaN/GaN light-emitting diodes on semipolar {11-22} GaN bulk substrates. Jpn. J. Appl. Phys., 45, L659-L662(2006).

    [26] S. Nakamura, M. Senoh, N. Iwasa, S. I. Nagahama. High-brightness InGaN blue, green and yellow light-emitting diodes with quantum well structures. Jpn. J. Appl. Phys., 34, L797-L799(1995).

    [27] F. Jiang, J. Zhang, L. Xu, J. Ding, G. Wang, X. Wu, X. Wang, C. Mo, Z. Quan, X. Guo, C. Zheng, S. Pan, J. Liu. Efficient InGaN-based yellow-light-emitting diodes. Photon. Res., 7, 144-148(2019).

    [28] F. Y. Jiang, Y. Pu. Bilayer inlet gas spray nozzle in use for metal-organic chemical vapor deposition device. China patent(2004).

    [29] J. D. Gao, J. L. Zhang, Z. J. Quan, S. Pan, J. L. Liu, F. Y. Jiang. Effect of horizontal p-n junction on optoelectronics characteristics in InGaN-based light-emitting diodes with V-shaped pits. J. Phys. D., 53, 335103(2020).

    [30] C. K. Li, C. K. Wu, C. C. Hsu, L. S. Lu, H. Li, T. C. Lu, Y. R. Wu. 3D numerical modeling of the carrier transport and radiative efficiency for InGaN/GaN light emitting diodes with V-shaped pits. AIP Adv., 6, 055208(2016).

    [31] Y. Li, F. Yun, X. Su, S. Liu, W. Ding, X. Hou. Deep hole injection assisted by large V-shape pits in InGaN/GaN multiple-quantum-wells blue light-emitting diodes. J. Appl. Phys., 116, 123101(2014).

    [32] T. Egawa, B. A. B. A. Shuhaimi. High performance InGaN LEDs on Si (1 1 1) substrates grown by MOCVD. J. Phys. D, 43, 354008(2010).

    [33] A. Hangleiter, F. Hitzel, C. Netzel, D. Fuhrmann, U. Rossow, G. Ade, P. Hinze. Suppression of nonradiative recombination by V-shaped pits in GaInN/GaN quantum wells produces a large increase in the light emission efficiency. Phys. Rev. Lett., 95, 127402(2005).

    [34] F. Jiang, J. Li, G. Q. Zhang, J. Zhang, Q. Sun, Z. Quan. GaN LEDs on Si substrate. Light-Emitting Diodes: Materials, Processes, Devices and Applications, 133-170(2019).

    [35] J. Liu, F. Feng, Y. Zhou, J. Zhang, F. Jiang. Stability of Al/Ti/Au contacts to N-polar n-GaN of GaN based vertical light emitting diode on silicon substrate. Appl. Phys. Lett., 99, 111112(2011).

    [36] F. Y. Jiang, J. L. Liu, J. L. Zhang, L. Q. Xu, J. Ding, G. X. Wang, Z. J. Quan, X. M. Wu, P. Zhao, B. Y. Liu, D. Li, X. L. Wang, C. D. Zheng, S. Pan, F. Fang, C. L. Mo. Semiconductor yellow light-emitting diodes. Acta Phys. Sin., 68, 168503(2019).

    [37] T. Y. Seong, J. I. Shim, J. Han, H. Amano, H. Morkoç. Internal quantum efficiency. III-Nitride Based Light Emitting Diodes and Applications, 163-207(2017).

    [38] K. G. Belyaev, M. V. Rakhlin, V. N. Jmerik, A. M. Mizerov, Y. V. Kuznetsova, M. V. Zamoryanskaya, S. V. Ivanov, A. A. Toropov. Phase separation in InxGa1-xN (0.10 < x < 0.40). Phys. Status Solidi C, 10, 527-531(2013).

    [39] T. Hikosaka, T. Shioda, Y. Harada, K. Tachibana, N. Sugiyama, S. Y. Nunoue. Impact of InGaN growth conditions on structural stability under high temperature process in InGaN/GaN multiple quantum wells. Phys. Status Solidi C, 8, 2016-2018(2011).

    [40] K. A. Bulashevich, O. V. Khokhlev, I. Y. Evstratov, S. Karpov. Simulation of light-emitting diodes for new physics understanding and device design. Proc. SPIE, 8278, 827819(2012).

    Shengnan Zhang, Jianli Zhang, Jiangdong Gao, Xiaolan Wang, Changda Zheng, Meng Zhang, Xiaoming Wu, Longquan Xu, Jie Ding, Zhijue Quan, Fengyi Jiang, "Efficient emission of InGaN-based light-emitting diodes: toward orange and red," Photonics Res. 8, 1671 (2020)
    Download Citation