• Photonics Research
  • Vol. 11, Issue 10, 1694 (2023)
Mauro David1, Davide Disnan2, Elena Arigliani1, Anna Lardschneider1, Georg Marschick1, Hanh T. Hoang1, Hermann Detz1、3, Bernhard Lendl4, Ulrich Schmid2, Gottfried Strasser1, and Borislav Hinkov1、*
Author Affiliations
  • 1Institute of Solid State Electronics and Center for Micro- and Nanostructures, TU Wien, Vienna, Austria
  • 2Institute of Sensor and Actuator Systems, TU Wien, Vienna, Austria
  • 3Central European Institute of Technology, Brno University of Technology, Brno, Czech Republic
  • 4Institute of Chemical Technologies and Analytics, Vienna, Austria
  • show less
    DOI: 10.1364/PRJ.495729 Cite this Article Set citation alerts
    Mauro David, Davide Disnan, Elena Arigliani, Anna Lardschneider, Georg Marschick, Hanh T. Hoang, Hermann Detz, Bernhard Lendl, Ulrich Schmid, Gottfried Strasser, Borislav Hinkov, "Advanced mid-infrared plasmonic waveguides for on-chip integrated photonics," Photonics Res. 11, 1694 (2023) Copy Citation Text show less

    Abstract

    Long-wave infrared (LWIR, 8–14 µm) photonics is a rapidly growing research field within the mid-IR with applications in molecular spectroscopy and optical free-space communication. LWIR applications are often addressed using rather bulky tabletop-sized free-space optical systems, preventing advanced photonic applications, such as rapid-time-scale experiments. Here, device miniaturization into photonic integrated circuits (PICs) with maintained optical capabilities is key to revolutionize mid-IR photonics. Subwavelength mode confinement in plasmonic structures enabled such miniaturization approaches in the visible-to-near-IR spectral range. However, adopting plasmonics for the LWIR needs suitable low-loss and -dispersion materials with compatible integration strategies to existing mid-IR technology. In this paper, we further unlock the field of LWIR/mid-IR PICs by combining photolithographic patterning of organic polymers with dielectric-loaded surface plasmon polariton (DLSPP) waveguides. In particular, polyethylene shows favorable optical properties, including low refractive index and broad transparency between 2 μm and 200 µm. We investigate the whole value chain, including design, fabrication, and characterization of polyethylene-based DLSPP waveguides and demonstrate their first-time plasmonic operation and mode guiding capabilities along S-bend structures. Low bending losses of 1.3 dB and straight-section propagation lengths of 1 mm, pave the way for unprecedented complex on-chip mid-IR photonic devices. Moreover, DLSPPs allow full control of the mode parameters (propagation length and guiding capabilities) for precisely addressing advanced sensing and telecommunication applications with chip-scale devices.

    1. INTRODUCTION

    The long-wave infrared (LWIR) spectral region (8–14 µm) is a portion of the electromagnetic spectrum covering many applications of significant interest, ranging from high-performance spectroscopy [14] to optical free-space communication [5]. In particular, chip-scale LWIR photonics has enormous potential for realizing unprecedented miniaturized devices. By specifically tailoring their characteristics, novel device concepts could be unlocked addressing, e.g., real-time reaction monitoring of (bio-)chemical samples [68], in situ health monitoring using (medical) wearables [3], and ultrafast optical data communication [911]. Although today’s most promising LWIR coherent light source, the quantum cascade laser (QCL) is commercially available, offering high power, room-temperature, and continuous-wave operation [1214], its monolithic counterpart, the QC detector (QCD), is currently still under development in this wavelength range [15,16]. In a first integration step, both can be combined into specifically tailored devices with same-wavelength emission and detection from the same active region [13,17,18], paving the way for a new class of monolithic photonic integrated circuits (PICs) [6,19]. However, in contrast to near-IR PICs with their high degree of maturity [20], mid-IR (2–20 µm) PICs are still in the early stages of development [21], and implementing existing integrated photonics solutions remains a challenging task [21,22]. It includes the requirement for new materials [23] and advanced fabrication schemes for developing low-loss and low-dispersion LWIR passive photonic structures on the chip level. Especially, concepts that allow efficient mode guiding and directing are currently lacking as crucial elements for fully integrated devices with versatile capabilities and complex functionalities. The primary obstacle in utilizing commonly used dielectrics for LWIR applications is their intrinsic absorption in this frequency range [22]. Although some dielectric waveguide solutions exist, their integration poses several challenges as these solutions often face compatibility issues with the active material system, need epitaxial regrowth processes, and they necessitate the scaling of geometrical parameters with the wavelength, further hindering their monolithic integration [24]. This is true, for example, for dielectric waveguides based on Ge [25,26], Si [27,28], halides [29], chalcogenides [30], or heavy metal oxides [31]. Nevertheless, recent work made noticeable progress by integrating InGaAs/InP passive dielectric waveguides with InP-based mid-IR QCLs with reported 2.2 dB/cm at 4.3 µm for homogeneous integration [24] and 1.2 dB/cm at 8 µm for monolithic integration [32]. However, this integration method requires a complex postregrowth fabrication scheme that can potentially decrease fabrication yield [33]. Another promising, and even simpler route for developing monolithic mid-IR PICs is presented by the use of dielectric-loaded surface plasmon polariton (DLSPP) waveguides [34,35]. They combine several advantages including tailorable propagation lengths and subwavelength mode confinement for further device miniaturization together with compatible available integration approaches.

    Plasmonic waveguides have several benefits over traditional dielectric waveguides, such as stronger mode confinement and higher field intensity [36,37]. They also exhibit enhanced light–matter interactions, making them promising candidates for applications in sensing [38], spectroscopy [39], and nonlinear optics [40]. Regarding fabrication, surface-plasmon polariton (SPP) waveguide-based devices benefit from using the same metal(s) for carrying optical signals as typically used for the electrical contacts of the device (e.g., Au). This simplifies their monolithic integration significantly [41]. Indeed, DLSPP waveguides based on 200–300 nm thick Si3N4 stripes on Au were already successfully demonstrated at 6.2  μm as linear optical couplers between QCL and QCD in novel mid-IR sensors [6,19,42]. However, the application of Si3N4 as a confinement layer is limited in the LWIR due to strong absorptions above 7 µm [43]. Moreover, the effective mode index of the presented structures (Neff1.008) is too low to provide efficient on-chip guiding, which is a necessity for more complex chip-scale optical circuits with advanced capabilities. Hereby, being able to guide an LWIR optical signal on a predefined path, potentially allows a much higher degree of control on the direction of the mode as compared to what could be achieved by controlling the light emission direction of individual discrete elements, such as QCLs [44].

    Despite providing broadband and low-loss transmission throughout the entire mid-IR spectrum (2–14 µm), similar limitations emerge for semiconductor-loaded SPP (SLSPP) waveguides based on, e.g., previously developed Ge/Au architectures [45]. Due to the broad transparency of germanium, it is possible to increase the Neff by appropriately tailoring the ridge cross section. However, this comes at the expense of a significantly lower propagation length [45]. Therefore, new materials are needed for the LWIR spectral range, providing high transparency and low refractive index (RI), thus, enabling similar performances as for their near-IR counterparts.

    Organic polymers have always been attractive candidates for such applications in PICs due to their low cost, biocompatibility, mechanical flexibility, low optical losses, ease of tunability, and compatibility with established nanofabrication processes [46,47]. Unfortunately, similar to many inorganic materials, the most commonly used polymers with excellent optical properties in the near IR, such as poly(methyl methacrylate) (PMMA) and SU-8, cannot be used at longer wavelengths since they strongly absorb in the LWIR region [48,49]. In contrast, polyethylene (PE) has recently been proposed as a promising material for mid-IR integrated photonics applications [50] based on its broad optical transparency (2200  μm) [50,51]. Methods to fabricate PE-based waveguides or antennas have already been reported for terahertz (THz) (>20  μm) applications [5254]. However, the lithographic surface patterning of PE films with micrometer resolution, necessary for the fabrication of high-precision chip-scale optical interconnects, was not reported so far. Moreover, the fundamental demonstration of LWIR plasmons in PE-based DLSPP waveguides was also not yet shown in literature.

    In this paper, we employ highly transparent PE films synthesized via spin coating as a ridge material for LWIR DLSPP waveguides. We use finite element simulations performed with the commercial software tool COMSOL to design and optimize various ridge geometries. We then fabricate the plasmonic devices by a novel UV-photolithographic process through the definition of an inorganic hard mask and O2 plasma etching. The device’s optical performance is experimentally studied, and the propagation losses are extracted using the cutback method. Our approach demonstrates the possibility of patterning PE to a wide variety of ridge geometries via a straightforward photolithography fabrication process. It enables full control of waveguide structures allowing to accurately tailor them to various dedicated applications. Besides demonstrating a new SPP waveguide system for the LWIR, we also unlock a new material platform for mid-to-far-IR integrated photonics. With this, we open an avenue for a new class of complex monolithic photonic devices and networks, exploiting the combination of PE-based waveguide structures with QC technology for the mid-IR and beyond.

    2. EXPERIMENTAL SECTION

    A. Simulation and Design of the Plasmonic Devices

    To carefully investigate the waveguiding properties of the PE-based DLSPP waveguides, we performed numerical simulations with the well-established optical mode solver of COMSOL Multiphysics. Based on the obtained RI data from our previous ellipsometry measurements available in literature [50], we carried out numerical mode analysis for a target wavelength of 9.26 µm. The simulation results served as design guidelines for the fabrication of the devices and for later estimation of the scattering losses caused by fabrication imperfections, such as structural defects and surface roughness. The figures of merit used as design parameters are the effective mode index Neff, propagation length Lp, and normalized area Aeff/A0. The propagation length is defined as Lp=1/(2α), where α is the attenuation constant. The normalized area is defined as the ratio between effective mode area Aeff and the diffraction limit A0=λ2/4, where Aeff=1Max{W(r)}AW(r)dAwith the energy density W(r) at position r, W(r)=12Re{d[ωε(r)]dω}|E(r)|2+12μ0|H(r)|2.

    B. Synthesis of the Polyethylene Films

    Amorphous PE films were spin coated in a humidity- and temperature-controlled glove box. The films were synthesized from linear low-density PE powder (Sigma-Aldrich, ρ=0.906  gmL1, average Mw35,000 and Mn7700) dispersed in toluene (Sigma-Aldrich, anhydrous, purity 99.8%) with a mass portion of 10%. The spin coating was conducted from a hot solution (100°C) at a rotation speed of 1000 r/min for 35 s with 5 s of acceleration using the dynamic dispense method. The samples were preheated to 120°C on a hotplate before spin coating and postbaked at 120°C for 15 min right after spin coating. Details about the synthesis of the films as well as their optical and structural characterization can be found in our previous work [50].

    C. Fabrication of Plasmonic Devices

    Double-side polished 2′′ Si (100) wafers with 275 µm thickness were used as substrates. After cleaving, the 11  mm×11  mm samples were ultrasonically cleaned in an acetone bath before the deposition of 8 nm of Ti and 100 nm of Au using a standard RF-sputtering machine (LS 320S, Von Ardenne). Subsequently, the polymer was spin coated on the Au-coated samples targeting a thickness of 5 µm. For patterning, AZ5214E photoresist was spin coated directly on top of the polymer at 4000 r/min for 30 s, followed by baking at 100°C for 1 min, resulting in a 1.5 µm thick resist layer. The resist was then patterned using a UV mask aligner (Karl Suess, MJB4) system for contact lithography with 4 s of exposure time, followed by 37 s of development in AZ726MIF. To transfer the pattern from the resist to the polymer, the sample was covered by a 100 nm Au layer (or 20 nm of Cr) deposited by electron-beam evaporation. After a lift-off procedure (30 min in acetone), the samples were etched using a plasma etching system (STS 320PC—no temperature control). The etching recipe used is based on a standard oxygen plasma (power: 150 W, O2 flow rate: 49.5 sccm, pressure: 150 mTorr, time: four cycles of 5 min etching followed by 10 min for cooling down) that can be further optimized to control the etch rate and sidewall roughness, and reduce redeposition on the substrate. The resulting etch rate was 250  nmmin1. The surface morphology of the fabricated devices will be discussed later. After the etching, a second lithography process is performed, similar as described above to remove the Au hard mask. Finally, the Au hard mask is etched using KI/I2 gold etchant for 30 s, and the resist is subsequently removed in an acetone bath. The fabrication process is shown later and can be improved by the use of a Cr hard mask, as described in Section 3. The final devices were prepared for optical characterization by cleaving them into different lengths.

    D. Transmission Measurements

    The devices were characterized in an end-fire coupling geometry using a custom-made setup consisting of a 2-lens geometry (C037TME-F, Thorlabs). The device under test was placed on a piezoelectric transition stage. The waveguides were tested at a wavelength of λ=9.26  μm using an HHL501 DFB-QCL. The laser light is directed to a mid-IR camera (Tau 2, Teledyne FLIR LLC, USA) for inspecting the beam profile and focused by a parabolic mirror onto a thermoelectrically cooled mercury cadmium telluride (MCT) detector (PVI-4TE-10.6, Vigo Systems S.A., Poland) through the use of a ZnSe beam splitter (BSW711, Thorlabs). To extract the waveguide losses, the effective cutback technique is used [45,5558]. The measurement procedure consists of inserting the waveguide between the lenses and carefully aligning the sample to maximize signal intensity. The reference measurement is taken prior to and after every reading, and the intensity of each waveguide is measured three times and averaged. The scattering losses from fabrication defects can then be calculated by subtracting the simulated propagation losses from the measured losses.

    3. RESULTS AND DISCUSSION

    A. Simulation and Design of the Plasmonic Structures

    The first step in the device design is based on performing simulations of various device structures conducted using the eigenmode solver of COMSOL Multiphysics. As the accuracy of the calculations strongly depends on the optical parameters of the materials involved, we optimized the thin-film fabrication technique to achieve high-quality layers with optical parameters similar to the bulk materials. Further details on the fabrication and the RI data of the PE thin films are available elsewhere [50]. The simulations were carried out for a target wavelength of 9.26 µm, which is in one of the spectral windows suitable for free-space optical telecommunication. The plasmonic waveguide architecture under investigation is the DLSPP waveguide, shown in Fig. 1(a). It consists of a dielectric ridge on top of a metal (Au) layer. Figure 1(b) shows the electric-field confinement (|Ey|) for a PE ridge of 3.6  μm×3.6  μm. For these design parameters, the mode is localized in the dielectric core of the waveguide at the metal-dielectric interface, showing good propagation length (LP455  μm) with an effective mode index of Neff=1.20. This demonstrates the promising performance characteristics of this material system for combining long-range LP with high enough Neff for potential optical mode guiding along the chip surface.

    (a) Cross section of the DLSPP waveguide. (b) |Ey| 2D-field profile of the TM00 SPP mode for a 3.6 μm×3.6 μm DLSPP waveguide at λ=9.26 μm. (c) Top view of the 3D simulation of the waveguide.

    Figure 1.(a) Cross section of the DLSPP waveguide. (b) |Ey| 2D-field profile of the TM00 SPP mode for a 3.6  μm×3.6  μm DLSPP waveguide at λ=9.26  μm. (c) Top view of the 3D simulation of the waveguide.

    Figure 2 shows the impact of the ridge dimensions on different figures of merit. Figure 2(a) displays the simulated effective mode index for different thicknesses, plotted over the ridge width. The figure highlights the value of Neff=1.1, yielding the minimum refractive index contrast to achieve effective mode guiding along waveguide bends in a surrounding cladding of air. For increasing ridge thicknesses, the Neff monotonously increases and enables better mode guiding capabilities. Figure 2(b) presents equivalent simulations, showing the impact of varying ridge dimensions on the propagation length LP. Overall, Fig. 2 demonstrates the typical trade-off for plasmonic waveguides where an increased Neff leads to increased mode confinement in the dielectric ridge at the expense of higher waveguide losses, i.e., lower LP. For thin ridge geometries (t<1.2  μm), the propagation length is on the order of 1 mm, however, Neff is too low to provide efficient mode guiding. Increasing the thickness of the ridge enlarges Neff and provides the necessary condition for light guiding, however, at the expense of the propagation length.

    (a) Mode effective index Neff for different ridge dimensions. (b) Propagation length Lp for different ridge dimensions.

    Figure 2.(a) Mode effective index Neff for different ridge dimensions. (b) Propagation length Lp for different ridge dimensions.

    These results show the similarity in terms of performance when comparing PE-based DLSPP waveguides with previously reported numerical studies for PMMA-based DLSPP waveguides at telecom frequencies [34].

    The above analysis of the geometrical factors performed via numerical simulations highlights specific ridge dimensions that are highly favorable for integrated photonics applications. In particular, Fig. 3(a) shows that there is an optimal ridge width (in the range of 2–5 µm) to minimize mode size, here expressed in the form of normalized mode area Aeff/A0. As in the case of PMMA-based DLSPP waveguides at telecom frequencies [59] for smaller-than-optimal ridge widths, the mode is pushed outside of the dielectric ridge, increasing its extension. For larger ridge widths, the mode will occupy all the available dielectric space leading again to a larger mode size [see also the inset in Fig. 7(b)]. Remarkably, for PE ridges with optimal geometries, the transmission performance can be highly comparable to the well-known PMMA-based DLSPP waveguides at telecom frequencies. This is shown in Fig. 3(b) where we simulated the transmission Tb=Ib/Ia [see the inset in Fig. 3(b)] for a 90° bend over a waveguide section of circular shape. For both, PE at λ=9.26  μm and PMMA at λ=1.55  μm, the reported transmission is displayed as a function of normalized radius R/λ [60]. The plot shows that the optical properties of both polymers at their respective operational wavelength are very similar and that by simply scaling the geometry, it is possible to reproduce the plasmonic performance of PMMA at telecom frequencies in PE for the LWIR spectral region. Using these simulation results as design guidelines, we proceeded with the fabrication of the plasmonic devices.

    (a) Influence of the PE ridge geometries on the effective mode area (Aeff/A0). (b) Comparison of the transmission (Ib/Ia) of a 90° PE DLSPP waveguide bend (cross section of 3.6 μm×3.6 μm) at λ=9.26 μm and a PMMA DLSPP waveguide (cross section of 600 nm×600 nm) at λ=1.55 μm as a function of its normalized radius (R/λ). Inset: 3D modeling of the PE waveguide mode.

    Figure 3.(a) Influence of the PE ridge geometries on the effective mode area (Aeff/A0). (b) Comparison of the transmission (Ib/Ia) of a 90° PE DLSPP waveguide bend (cross section of 3.6  μm×3.6  μm) at λ=9.26  μm and a PMMA DLSPP waveguide (cross section of 600  nm×600  nm) at λ=1.55  μm as a function of its normalized radius (R/λ). Inset: 3D modeling of the PE waveguide mode.

    B. Fabrication of the Plasmonic Devices

    Gold is one of the most commonly used metals for electrical contacts of mid-to-far IR photonic devices, making it a suitable choice for plasmonic layers as discussed previously. Another important benefit of employing metal-based plasmonics is the independency from the substrate material, allowing a much more flexible integration. In other words, it provides greater flexibility in the choice of substrate material for the photonic device. Indeed, the penetration depth of the evanescent field into the metal for LWIR frequencies amounts to only around 13 nm. This enabled the use of Si substrates coated with a 100 nm plasmonic Au layer, whereas, QC technology-based material systems, such as InP or GaAs can also be used. The PE films used as core material for the DLSPP waveguides were deposited by spin coating from a solution of concentration (mass fraction) of 10%, resulting in films of 5.0 µm thickness. For the targeted wavelength of 9.26 µm, the real and imaginary parts of the refractive index of the PE films were measured with ellipsometry [50] and found to be 1.48 and 0.0001, respectively. Figure 4 shows the schematic flowchart of the fabrication steps of the plasmonic devices. As PE is not inherently a UV-sensitive polymer [61], we used a similar approach that has been used for organic PVDF-based microelectromechanical systems [62], i.e., by definition of an inorganic hard mask. In the case of an Au hard mask [Fig. 4(a)], the lithographic process must be repeated a second time in order to safely remove the top Au layer without damaging the one at the bottom. In the following attempts, the fabrication technique was further optimized using a Cr hard mask [Fig. 4(b)], which significantly reduced the number of “mouse-bite-type” defects at the bottom of the waveguide because the Cr etchant does not attack the bottom Au layer. As an additional advantage, this also avoids the need for a second lithography step. Further details on the film and ridge fabrication can be found in the Section 2. After the device fabrication, the chips were finalized by cleaving the plasmonic waveguides into different lengths (ranging from 1 mm to 2.3 mm) for cutback measurements.

    Schematic flow chart of the chip fabrication process, (a) using an Au hard mask and (b) using a Cr hard mask.

    Figure 4.Schematic flow chart of the chip fabrication process, (a) using an Au hard mask and (b) using a Cr hard mask.

    The surface topography of the spin-coated thin films was then characterized using an atomic force microscope (AFM). Figure 5 shows the root-mean-square (rms) area roughness of the PE layer after spin coating. The rms roughness of the PE layer was found to be 10.4 nm, suggesting a relatively smooth surface as a result of the spin-coating process. Notably, no significant difference in surface topography was observed between the top of the fabricated devices and the spin-coated films prior to surface patterning (Sq=10.7  nm).

    Typical AFM image of the fabricated PE films right after spin coating. rms area roughness amounts to Sq=10.4 nm.

    Figure 5.Typical AFM image of the fabricated PE films right after spin coating. rms area roughness amounts to Sq=10.4  nm.

    Following fabrication, the structures were analyzed with a scanning electron microscope (SEM) to evaluate their physical characteristics (Fig. 6). The SEM images revealed that the sidewalls of the waveguide exhibited a certain degree of roughness that can potentially lead to increased scattering losses and reduced efficiency of the device. However, the upper waveguide edge appeared to be relatively flat, indicating that the fabrication process was able to achieve a good level of precision.

    Scanning electron microscope (SEM) image of a DLSPP PE-waveguide structure. (a) Plasmonic waveguide and (b) Closeup of the 8 µm wide and 1 µm high PE stripe.

    Figure 6.Scanning electron microscope (SEM) image of a DLSPP PE-waveguide structure. (a) Plasmonic waveguide and (b) Closeup of the 8 µm wide and 1 µm high PE stripe.

    Several geometries were investigated varying the widths from 3 µm to 20 µm. The devices were etched using a plasma etching system (STS 320PC—without implemented temperature control). After the plasma etching process, we observed an inhomogeneous decrease in thickness after each etching step. As the polymer has a relatively low melting point (110°C–135°C), we attribute this to the uncontrolled temperature reached in the chamber combined with the low pressure during the etching process. In particular, devices fabricated with a 20 nm Cr hard mask, as opposed to 100 nm of Au, exhibited a minor decrease in thickness, indicating that the polymeric films potentially reached the softening point (110°C) during the etching process and were affected by the weight of the hard mask. However, because of these unexpected changes in thicknesses, we obtained devices with wider variety of geometrical parameters, allowing us to perform a much more general and complete comparison of the experimental results with the theoretically predicted ones.

    C. Transmission Measurements

    The optical performance of the plasmonic devices was determined by transmission measurements using a custom-built measurement setup [45]. The propagation losses were determined by the effective cutback method for each fabricated waveguide geometry [5558]. The summary of the results in terms of waveguide and coupling losses is shown in Fig. 7(a). The fabricated devices were modeled in COMSOL, and the losses and normalized area results are displayed as dashed lines. The deviation between the measured data of Fig. 7(a) with the model can be attributed to fabrication imperfections leading to differences in device performance. Overall the measurements show excellent agreement with simulations. Figure 7(b) shows the corresponding mode cross sections for the different dimensions.

    (a) Summary of measured data in terms of waveguide losses (left) and coupling losses (right) extracted from the effective cutback method. The square points represent the losses extracted with the cutback method per each waveguide width. Dashed lines represent the exponential fit of the results obtained from the simulations. (b) Mode-profile simulations of the fabricated DLSPP waveguides, indicating their respective width (w) and thickness (t) measured with a profilometer.

    Figure 7.(a) Summary of measured data in terms of waveguide losses (left) and coupling losses (right) extracted from the effective cutback method. The square points represent the losses extracted with the cutback method per each waveguide width. Dashed lines represent the exponential fit of the results obtained from the simulations. (b) Mode-profile simulations of the fabricated DLSPP waveguides, indicating their respective width (w) and thickness (t) measured with a profilometer.

    In SPP waveguides, the supported vertical and lateral mode confinements are strongly dependent on geometrical factors as depicted in Fig. 7(b). This relationship is experimentally validated by comparing measured coupling losses with the simulated normalized effective mode area (Aeff/A0). In an end-fire coupling experiment, coupling losses occur when the input light mode is not perfectly matched to the mode size supported by the receiving optical component. Hence, larger effective mode areas lead to higher coupling losses (for lenses with small focal spot sizes as in this case) since the spatial overlap between the lens and waveguide mode is reduced. Conversely, smaller effective mode areas result in lower coupling losses due to the higher spatial overlap between the two components. In conclusion, our measurements fit well with the simulation results.

    The lower RI of this polymer allows for the first-time replicating of a similar DLSPP waveguide performance in the LWIR as compared to PMMA at telecom wavelengths. In contrast, the implementation of transparent high-RI materials, such as Si or Ge, requires the use of much smaller geometries (width and thickness approximately 1  μm×1  μm) to achieve similar routing performances. However, in the latter case, achieving such low-loss propagation is not feasible due to the higher degree of confinement that amplifies the losses of the optical mode because of the lossy Au layer. Moreover, their fabrication and integration with active devices on the same chip can be challenging with such small dimensions.

    Table 1 presents a comprehensive comparison of experimentally realized mid-IR plasmonic waveguide platforms based on plasmonic structures. The table illustrates that PE is capable of achieving similar performance above 9 µm wavelength as SiNx does up to 6.5  μm, particularly, below the onset of its absorption band [43]. Importantly, our paper introduces the first mid-IR plasmonic platform with mode guiding capabilities.

    Comparison of Mid-IR Plasmonic Waveguide Platforms

    Waveguide PlatformWavelength (µm)Propagation Length (mm)Attenuation (dB/mm)Mode Guiding CapabilitiesReferences
    60 µm wide gold stripe7.51.82.41No[63]c
    15 µm wide and 200 nm thick SiNx stripe on Au6.52–42.1–1.1No[19]a
    15 µm wide and 200 nm thick SiNx stripe on Au6.11.72.55No[6]a,b
    6.21.82.41
    9 µm wide and 300 nm thick Ge stripe on Au9.120.6456.73No[45]c
    5 µm wide and 450 nm thick PE stripe on Au9.2622.5NoThis paper
    5 µm wide and 3 µm thick PE ridge on Au9.260.3111–3 dB (90° bend with 26 µm radius)YesThis paper

    From simulations.

    Tapered waveguide.

    Experimentally determined losses.

    (a) SEM images of the S-bend structures (width w=5 μm and thickness t=3 μm) with an offset of d=75 μm. (b) S-bend transmission dependence on the offset distance between the two arms (Sections A and B) obtained by numerical modeling and measurements. The inset shows the top view of the 3D simulations for offsets of d=24 μm and d=96 μm.

    Figure 8.(a) SEM images of the S-bend structures (width w=5  μm and thickness t=3  μm) with an offset of d=75  μm. (b) S-bend transmission dependence on the offset distance between the two arms (Sections A and B) obtained by numerical modeling and measurements. The inset shows the top view of the 3D simulations for offsets of d=24  μm and d=96  μm.

    The findings of this paper carry significant implications for the development of organic-based biocompatible photonic integration concepts utilizing plasmonic or other photonic waveguide designs for the LWIR, including traditional dielectric or photonic crystals waveguides and optical fibers. Therefore, the demonstrated low-loss properties of the PE utilized in this paper and its successful fabrication present a highly promising path toward realizing fully integrated and complex photonic systems. Furthermore, the success of the UV-lithography process used to pattern PE films offers new possibilities for the realization of other low-loss photonic waveguide architectures in the mid-to-far-IR range. In addition, the same fabrication routine can be used to create transparent microfluidic chips with micrometer feature size, offering a new platform for on-chip fluidic transport and optical sensing. This approach could be used to develop fully integrated lab-on-a-chip systems that are largely transparent in both the visible and the mid-IR, whereas, unlocking a wide range of biological and chemical sensing applications. Additionally, it can enable the development of novel low-loss waveguide architectures for applications beyond the LWIR and in the THz range.

    4. CONCLUSION

    We have realized the first demonstration of PE-based plasmonic waveguides in the LWIR. This opens the much-needed pathway for realizing more complex LWIR monolithic PICs and networks on the chip-scale with a wide variety of tailorable properties. After spin coating of the organic PE thin films, a suitable fabrication process using plasma etching and a metallic hard mask was developed to pattern the plasmonic structures. Transmission measurements show good agreement with simulations in terms of waveguide losses. From the experiments, the measured waveguide propagation losses of the fabricated devices lie between 0.00248 and 0.01545dB  μm1 and bend losses are 1.32.3  dB. These values can be further improved by optimizing the fabrication process. The promising material properties of this polymer will open new pathways for organic-based integrated photonic devices. They are not limited to plasmonic concepts and offer the coverage of a broad spectral range from mid- to-far infrared frequencies.

    Acknowledgment

    Acknowledgment. We acknowledge received funding from the EU Horizon 2020 Framework Program, B.H. acknowledges funding by the Austrian Science Fund FWF. CzechNanoLab project funded by MEYS CR is gratefully acknowledged for the financial support of the measurements at CEITEC Nano Research Infrastructure. Fruitful discussions with W. Schrenk, A. M. Andrews, and B. Schwarz are gratefully acknowledged. We want to thank A. Dabrowska, S. Dal Cin, I. C. Doganlar, and A. Linzer for expert technical assistance.

    References

    [1] S. S. Brown. Absorption spectroscopy in high-finesse cavities for atmospheric studies. Chem. Rev., 103, 5219-5238(2003).

    [2] M. E. Webber, M. Pushkarsky, C. K. N. Patel. Optical detection of chemical warfare agents and toxic industrial chemicals: simulation. J. Appl. Phys., 97, 113101(2005).

    [3] R. Kasahara, S. Kino, S. Soyama, Y. Matsuura. Noninvasive glucose monitoring using mid-infrared absorption spectroscopy based on a few wavenumbers. Biomed. Opt. Express, 9, 289-302(2018).

    [4] I. L. Jernelv, K. Milenko, S. S. Fuglerud, D. R. Hjelme, R. Ellingsen, A. Aksnes. A review of optical methods for continuous glucose monitoring. Appl. Spectrosc. Rev., 54, 543-572(2019).

    [5] L. Flannigan, L. Yoell, C.-q. Xu. Mid-wave and long-wave infrared transmitters and detectors for optical satellite communications—a review. J. Opt., 24, 043002(2022).

    [6] B. Hinkov, F. Pilat, L. Lux, P. L. Souza, M. David, A. Schwaighofer, D. Ristanić, B. Schwarz, H. Detz, A. M. Andrews, B. Lendl, G. Strasser. A mid-infrared lab-on-a-chip for dynamic reaction monitoring. Nat. Commun., 13, 4753(2022).

    [7] A. Dabrowska, A. Schwaighofer, S. Lindner, B. Lendl, B. Lendl. Mid-IR refractive index sensor for detecting proteins employing an external cavity quantum cascade laser-based Mach-Zehnder interferometer. Opt. Express, 28, 36632-36642(2020).

    [8] A. Dabrowska, M. David, S. Freitag, A. M. Andrews, G. Strasser, B. Hinkov, A. Schwaighofer, B. Lendl. Broadband laser-based mid-infrared spectroscopy employing a quantum cascade detector for milk protein analysis. Sens. Actuators B, 350, 130873(2022).

    [9] R. Martini, E. A. Whittaker. Quantum cascade laser-based free space optical communications. J. Opt. Fiber Commun. Rep., 2, 279-292(2005).

    [10] X. Pang, O. Ozolins, L. Zhang, R. Schatz, A. Udalcovs, X. Yu, G. Jacobsen, S. Popov, J. Chen, S. Lourdudoss. Free-space communications enabled by quantum cascade lasers. Phys. Status Solidi A, 218, 2000407(2021).

    [11] H. Dely, T. Bonazzi, O. Spitz, E. Rodriguez, D. Gacemi, Y. Todorov, K. Pantzas, G. Beaudoin, I. Sagnes, L. Li, A. G. Davies, E. H. Linfield, F. Grillot, A. Vasanelli, C. Sirtori. 10 Gbit s−1 free space data transmission at 9 μm wavelength with unipolar quantum optoelectronics. Laser Photon. Rev., 16, 2100414(2022).

    [12] Q. Y. Lu, Y. Bai, N. Bandyopadhyay, S. Slivken, M. Razeghi. 2.4 W room temperature continuous wave operation of distributed feedback quantum cascade lasers. Appl. Phys. Lett., 98, 181106(2011).

    [13] B. Schwarz, C. A. Wang, L. Missaggia, T. S. Mansuripur, P. Chevalier, M. K. Connors, D. McNulty, J. Cederberg, G. Strasser, F. Capasso. Watt-level continuous-wave emission from a bifunctional quantum cascade laser/detector. ACS Photon., 4, 1225-1231(2017).

    [14] H. Knötig, B. Hinkov, R. Weih, S. Höfling, J. Koeth, G. Strasser. Continuous-wave operation of vertically emitting ring interband cascade lasers at room temperature. Appl. Phys. Lett., 116, 131101(2020).

    [15] A. Delga. Quantum cascade detectors: a review. Mid-Infrared Optoelectronics, 337-377(2020).

    [16] G. Marschick, M. David, E. Arigliani, N. Opačak, B. Schwarz, M. Giparakis, A. Delga, M. Lagree, T. Poletti, V. Trinite, A. Evirgen, B. Gerard, G. Ramer, R. Maulini, J. Butet, S. Blaser, A. M. Andrews, G. Strasser, B. Hinkov. High-responsivity operation of quantum cascade detectors at 9 μm. Opt. Express, 30, 40188-40195(2022).

    [17] B. Schwarz, P. Reininger, H. Detz, T. Zederbauer, A. M. Andrews, S. Kalchmair, W. Schrenk, O. Baumgartner, H. Kosina, G. Strasser. A bi-functional quantum cascade device for same-frequency lasing and detection. Appl. Phys. Lett., 101, 191109(2012).

    [18] B. Schwarz, D. Ristanic, P. Reininger, T. Zederbauer, D. MacFarland, H. Detz, A. M. Andrews, W. Schrenk, G. Strasser. High performance bi-functional quantum cascade laser and detector. Appl. Phys. Lett., 107, 071104(2015).

    [19] B. Schwarz, P. Reininger, D. Ristanić, H. Detz, A. M. Andrews, W. Schrenk, G. Strasser. Monolithically integrated mid-infrared lab-on-a-chip using plasmonics and quantum cascade structures. Nat. Commun., 5, 4085(2014).

    [20] R. Soref. The past, present, and future of silicon photonics. IEEE J. Sel. Top. Quantum Electron., 12, 1678-1687(2006).

    [21] H. Lin, Z. Luo, T. Gu, L. C. Kimerling, K. Wada, A. Agarwal, J. Hu. Mid-infrared integrated photonics on silicon: a perspective. J. Nanophotonics, 7, 393-420(2018).

    [22] A. Yadav, A. M. Agarwal. Integrated photonic materials for the mid-infrared. Int. J. Appl. Glass Sci., 11, 491-510(2020).

    [23] V. M. Lavchiev, B. Jakoby. Photonics in the mid-infrared: challenges in single-chip integration and absorption sensing. IEEE J. Sel. Top. Quantum Electron., 23, 452-463(2017).

    [24] S. Jung, D. Palaferri, K. Zhang, F. Xie, Y. Okuno, C. Pinzone, K. Lascola, M. A. Belkin. Homogeneous photonic integration of mid-infrared quantum cascade lasers with low-loss passive waveguides on an InP platform. Optica, 6, 1023-1030(2019).

    [25] A. Osman, M. Nedeljkovic, J. S. Penades, Y. Wu, Z. Qu, A. Z. Khokhar, K. Debnath, G. Z. Mashanovich. Suspended low-loss germanium waveguides for the longwave infrared. Opt. Lett., 43, 5997-6000(2018).

    [26] Y.-C. Chang, V. Paeder, L. Hvozdara, J.-M. Hartmann, H. P. Herzig. Low-loss germanium strip waveguides on silicon for the mid-infrared. Opt. Lett., 37, 2883-2885(2012).

    [27] J. S. Penadés, A. Sánchez-Postigo, M. Nedeljkovic, A. Ortega-Moñux, J. G. Wangüemert-Pérez, Y. Xu, R. Halir, Z. Qu, A. Z. Khokhar, A. Osman, W. Cao, C. G. Littlejohns, P. Cheben, I. Molina-Fernández, G. Z. Mashanovich. Suspended silicon waveguides for long-wave infrared wavelengths. Opt. Lett., 43, 795-798(2018).

    [28] J.-M. Fedeli, S. Nicoletti. Mid-infrared (mid-IR) silicon-based photonics. Proc. IEEE, 106, 2302-2312(2018).

    [29] T. Lewi, A. Katzir. Silver halide single-mode strip waveguides for the mid-infrared. Opt. Lett., 37, 2733-2735(2012).

    [30] A. Gutierrez-Arroyo, E. Baudet, L. Bodiou, J. Lemaitre, I. Hardy, F. Faijan, B. Bureau, V. Nazabal, J. Charrier. Optical characterization at 7.7 μm of an integrated platform based on chalcogenide waveguides for sensing applications in the mid-infrared. Opt. Express, 24, 23109-23117(2016).

    [31] C. Xin, H. Wu, Y. Xie, S. Yu, N. Zhou, Z. Shi, X. Guo, L. Tong. CdTe microwires as mid-infrared optical waveguides. Opt. Express, 26, 10944-10952(2018).

    [32] R. Wang, P. Täschler, Z. Wang, E. Gini, M. Beck, J. Faist. Monolithic integration of mid-infrared quantum cascade lasers and frequency combs with passive waveguides. ACS Photon., 9, 426-431(2022).

    [33] M. R. Billah, M. Blaicher, T. Hoose, P.-I. Dietrich, P. Marin-Palomo, N. Lindenmann, A. Nesic, A. Hofmann, U. Troppenz, M. Moehrle, S. Randel, W. Freude, C. Koos. Hybrid integration of silicon photonics circuits and InP lasers by photonic wire bonding. Optica, 5, 876-883(2018).

    [34] T. Holmgaard, S. I. Bozhevolnyi. Theoretical analysis of dielectric-loaded surface plasmon-polariton waveguides. Phys. Rev. B, 75, 245405(2007).

    [35] T. Holmgaard, S. I. Bozhevolnyi, L. Markey, A. Dereux. Dielectric-loaded surface plasmon-polariton waveguides at telecommunication wavelengths: excitation and characterization. Appl. Phys. Lett., 92, 011124(2008).

    [36] H.-S. Chu, P. Bai, E.-P. Li, W. R. J. Hoefer. Hybrid dielectric-loaded plasmonic waveguide-based power splitter and ring resonator: compact size and high optical performance for nanophotonic circuits. Plasmonics, 6, 591-597(2011).

    [37] S. Law, V. Podolskiy, D. Wasserman. Towards nano-scale photonics with micro-scale photons: the opportunities and challenges of mid-infrared plasmonics. J. Nanophotonics, 2, 103-130(2013).

    [38] J. Divya, S. Selvendran, A. S. Raja, A. Sivasubramanian. Surface plasmon based plasmonic sensors: a review on their past, present and future. Biosens. Bioelectron. X, 11, 100175(2022).

    [39] X. Wang, S.-C. Huang, S. Hu, S. Yan, B. Ren. Fundamental understanding and applications of plasmon-enhanced Raman spectroscopy. Nat. Rev. Phys., 2, 253-271(2020).

    [40] N. C. Panoiu, W. E. I. Sha, D. Y. Lei, G.-C. Li. Nonlinear optics in plasmonic nanostructures. J. Opt., 20, 083001(2018).

    [41] A. Kumar, J. Gosciniak, V. S. Volkov, S. Papaioannou, D. Kalavrouziotis, K. Vyrsokinos, J.-C. Weeber, K. Hassan, L. Markey, A. Dereux, T. Tekin, M. Waldow, D. Apostolopoulos, H. Avramopoulos, N. Pleros, S. I. Bozhevolnyi. Dielectric-loaded plasmonic waveguide components: going practical. Laser Photon. Rev., 7, 938-951(2013).

    [42] F. Pilat, B. Schwarz, B. Baumgartner, D. Ristanić, H. Detz, A. M. Andrews, B. Lendl, G. Strasser, B. Hinkov. Beyond Karl Fischer titration: a monolithic quantum cascade sensor for monitoring residual water concentration in solvents. Lab Chip, 23, 1816-1824(2023).

    [43] J. Kischkat, S. Peters, B. Gruska, M. Semtsiv, M. Chashnikova, M. Klinkmüller, O. Fedosenko, S. Machulik, A. Aleksandrova, G. Monastyrskyi, Y. Flores, W. T. Masselink. Mid-infrared optical properties of thin films of aluminum oxide, titanium dioxide, silicon dioxide, aluminum nitride, and silicon nitride. Appl. Opt., 51, 6789-6798(2012).

    [44] B. Hinkov, F. Fuchs, W. Bronner, K. Kohler, J. Wagner. Current- and temperature-induced beam steering in 7.8-μm emitting quantum-cascade lasers. IEEE J. Quantum Electron., 44, 1124-1128(2008).

    [45] M. David, A. Dabrowska, M. Sistani, I. C. Doganlar, E. Hinkelmann, H. Detz, W. M. Weber, B. Lendl, G. Strasser, B. Hinkov. Octave-spanning low-loss mid-IR waveguides based on semiconductor-loaded plasmonics. Opt. Express, 29, 43567-43579(2021).

    [46] H. Ma, A. K.-Y. Jen, L. R. Dalton. Polymer-based optical waveguides: materials, processing, and devices. Adv. Mater., 14, 1339-1365(2002).

    [47] J. Clark, G. Lanzani. Organic photonics for communications. Nat. Photonics, 4, 438-446(2010).

    [48] S. Tsuda, S. Yamaguchi, Y. Kanamori, H. Yugami. Spectral and angular shaping of infrared radiation in a polymer resonator with molecular vibrational modes. Opt. Express, 26, 6899-6915(2018).

    [49] E. Motaharifar, R. G. Pierce, R. Islam, R. Henderson, J. W. P. Hsu, M. Lee. Broadband terahertz refraction index dispersion and loss of polymeric dielectric substrate and packaging materials. J. Infrared Millim. THz Waves, 39, 93-104(2018).

    [50] M. David, D. Disnan, A. Lardschneider, D. Wacht, H. T. Hoang, G. Ramer, H. Detz, B. Lendl, U. Schmid, G. Strasser, B. Hinkov. Structure and mid-infrared optical properties of spin-coated polyethylene films developed for integrated photonics applications. Opt. Mater. Express, 12, 2168-2180(2022).

    [51] D. R. Smith, E. V. Loewenstein. Optical constants of far infrared materials. 3: plastics. Appl. Opt., 14, 1335-1341(1975).

    [52] M. Geiger, M. Hitzler, J. Iberle, C. Waldschmidt. A dielectric lens antenna fed by a flexible dielectric waveguide at 160 GHz. 11th European Conference on Antennas and Propagation (EUCAP), 3380-3383(2017).

    [53] H. I. Song, H. Jin, H.-M. Bae. Plastic straw: future of high-speed signaling. Sci. Rep., 5, 16062(2015).

    [54] B. You, J.-Y. Lu, T.-A. Liu, J.-L. Peng. Hybrid terahertz plasmonic waveguide for sensing applications. Opt. Express, 21, 21087-21096(2013).

    [55] P. Berini, R. Charbonneau, N. Lahoud, G. Mattiussi. Characterization of long-range surface-plasmon-polariton waveguides. J. Appl. Phys., 98, 043109(2005).

    [56] S.-T. Huang, C.-C. Lai, F.-W. Sheu, W.-S. Tsai. Characterization of long-range plasmonic waveguides at visible to near-infrared regime. AIP Adv., 7, 125221(2017).

    [57] T. Nikolajsen, K. Leosson, I. Salakhutdinov, S. I. Bozhevolnyi. Polymer-based surface-plasmon-polariton stripe waveguides at telecommunication wavelengths. Appl. Phys. Lett., 82, 668-670(2003).

    [58] R. Zektzer, B. Desiatov, N. Mazurski, S. I. Bozhevolnyi, U. Levy. Experimental demonstration of CMOS-compatible long-range dielectric-loaded surface plasmon-polariton waveguides (LR-DLSPPWs). Opt. Express, 22, 22009-22017(2014).

    [59] A. V. Krasavin, A. V. Zayats. Active nanophotonic circuitry based on dielectric-loaded plasmonic waveguides. Adv. Opt. Mater., 3, 1662-1690(2015).

    [60] B. Steinberger, A. Hohenau, H. Ditlbacher, F. R. Aussenegg, A. Leitner, J. R. Krenn. Dielectric stripes on gold as surface plasmon waveguides: bends and directional couplers. Appl. Phys. Lett., 91, 081111(2007).

    [61] K. Q. Nguyen, P. Cousin, K. Mohamed, M. Robert, A. El-Safty, B. Benmokrane. Effects of ultraviolet radiation on recycled and virgin HDPE corrugated pipes used in road drainage systems. J. Polym. Environ., 30, 3391-3408(2022).

    [62] J. Hafner, M. Teuschel, J. Schrattenholzer, M. Schneider, U. Schmid. Optimized batch process for organic MEMS devices. Proceedings, 2, 904(2018).

    [63] J.-P. Tetienne, A. Bousseksou, D. Costantini, R. Colombelli, A. Babuty, I. Moldovan-Doyen, Y. De Wilde, C. Sirtori, G. Beaudoin, L. Largeau, O. Mauguin, I. Sagnes. Injection of midinfrared surface plasmon polaritons with an integrated device. Appl. Phys. Lett., 97, 211110(2010).

    Mauro David, Davide Disnan, Elena Arigliani, Anna Lardschneider, Georg Marschick, Hanh T. Hoang, Hermann Detz, Bernhard Lendl, Ulrich Schmid, Gottfried Strasser, Borislav Hinkov, "Advanced mid-infrared plasmonic waveguides for on-chip integrated photonics," Photonics Res. 11, 1694 (2023)
    Download Citation